AISI 1513 Carbon Steel Plate, AISI 1513 Sheet, AISI 1513 Flat Bar, AISI 1513 Round Bar,AISI 1513 Suppliers

March 26, 2018 | Author: Carmen Servigna | Category: Structural Steel, Steel, Alloy, Annealing (Metallurgy), Materials Science


Comments



Description

9/2/2017 AISI 1513 Carbon steel plate, AISI 1513 sheet, AISI 1513 flat bar, AISI 1513 round bar,AISI 1513 suppliersSite Map | Text only | XML | Contact Home | Profile | Products | Equipment | steel base | Quote | FAQ | Contact us | Message | 9 Products   search Current Location:Home » Products » Carbon steel » AISI 1513 PRODUCT CATEGORY AISI 1513 Stainless Steel DATA TABLE FOR:PRODUCTS: CARBON STEEL:AISI 1513 Mould steel AISI 1513 properties and heat treatment forged piece, Including AISI 1513 application and specifications, We have all specifications,Including AISI 1513 steel plate, AISI 1513 sheet, AISI 1513 square steel, AISI 1513 flat bar,AISI 1513 Heat resistant steel round bar,AISI 1513 forgings, we can own production and sales. Tool steel Bearing steel Hastelloy Distributor Plate,Sheet,Bar,Pipe,Tubing,Wire American Special Metals, Corp. Go to Spring steel americanspecialmetals.com Alloy steel Introduction to Our Products: Nickel base alloy and Specialized high quality steel high nickel containing Cementation steels We have the advantages of equipment, technologies and price forged/hot rolling/ extrusion of steel steels Free­cutting steels We can produce the AISI 1513 has the following specifications: Cold extrusion steels Round bar steel: 1mm to 3000mm Nitriding steels Square­shape steel: 1mm to 2000mm Plate steel:0.1mm to 2500mm Chain steels Width: 10mm to 2500mm Lenth: We can supply any lenth based on the customer's requirement. Carbon steel Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes Ti Alloy Tubings: OD: φ6­219 mm, with wall thickness ranging from 1­35 mm. Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions High temperature high based on the customer's requirement Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement strength alloy and high­ Low alloy high­ Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode. temperature alloy temperature steel Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price. We serve you with our honesty, integrity, and professionality. Hastelloy Distributor Plate,Sheet,Bar,Pipe,Tubing,Wire American Special Metals, Corp. Go to americanspecialmetals.com Chemical composition % of the ladle analysis of grade AISI 1513 and Standards Category  steel Class  Carbon steel Type  Standard Designations  United States: UNS G15130 Composition Element Weight % C  0.10­0.16  Mn  1.10­1.40  P  0.04 (max)  S  0.05 (max)  Mechanical Properties  Conditions  Properties T (°C) Treatment Density (×1000 kg/m3) 7.7­8.03 25   Poisson's Ratio 0.27­0.30 25   Elastic Modulus (GPa) 190­210 25   seamless pipe manufacture profession steel pipe factory ASME,JIS,DIN,GOST standard Go to strpipe.com http://www.steel0.com/AISI_1513.htm#AISI 1513 Mechanical Performance Report 1/2 Download >> Principal Design Features One of the most widely used precipitation hardening grades in the business. It can be machined in the annealed condition. Post­work solution treatment is required prior to final hardening.9/2/2017 AISI 1513 Carbon steel plate. Forging Soak for 1 hour at 2150 F (1177 C) prior to forging.AISI 1513 suppliers Machining performance Download AISI 1513 the mechanical properties of the report. AISI 1513 sheet. Heat Treatment CONDITION A­­Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. AISI 1513 square steel. Do not work below 1850 F (1010 C). H1075.htm#AISI 1513 Mechanical Performance Report 2/2 .AISI 1513 forgings Copyright © 1996­2011 Longhai Special Steel. Machinability Long. While soft and ductile in the solution annealed condition. CONDITION H925.com Stainless Steel | Mould steel | Heat resistant steel | Tool steel | Bearing steel | Spring steel | Alloy steel | Nickel base alloy and high nickel containing steels | Cementation steels | Free­cutting steels | Cold extrusion steels | Nitriding steels | Chain steels | Carbon steel | Ti Alloy | High temperature high strength alloy and high­temperature alloy | Low alloy high­temperature steel | http://www.steel0. AISI 1513 sheet.AISI 1513 round bar. H1100. Longhai steel is China's special steel inventory spot suppliers. air cool.com/AISI_1513. then re­heat to 1150 F (620 C) for 4 hours and air cool. air cool. the report provides detailed performance analysis and application. however condition H1150M will yield best results. CONDITION H 950­ Treat Condition A material at 900 F(482 C) for 1 hour. All Rights Reserved. high harness. gummy chips characterize this alloys machinability. it is capable of high properties with a single precipitation or aging treatment.  Telephone: +86­816­3646575 Facsimile: +86­816­3639422 E­mail:sales@steel0. this alloy should not be joined by oxyacetylene welding. AISI 1513 round bar. H1150­ Soak solution treated material for 4 hours at specified temperature. Hot tags:AISI 1513 steel plate. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition. toughness and strength. H1025. AISI 1513 flat bar. air cool. AISI 1513 flat bar. CONDITION H1150M­ Soak solution treated material at 1400 F (760 C) for 2 hours. AWS E/ER630 filler metal is recommended if required. Welding Successfully welded by common fusion and resistance methods.. Characterized by good corrosion resistance.
Copyright © 2024 DOKUMEN.SITE Inc.