401160 Henkel Aero Structural Adhesives Products

Structural AdhesivesAerospace Product Selector Guide Structural Adhesives | 3 Structural Adhesives Metal & Honeycomb Bonding | p. 6 Film Adhesives | p. 4 Composites Bonding and Repair | p. 10 Syntactic, Core Fill and Abradable | p. 18 Composite Surface Preparation | p. 14 Surfacing & Lightning Strike Protection | p. 16 Primers | p. 24 Structural Adhesives Metal, Honeycomb Paste Adhesives | p. 26 Bonding & Repair | p. 28 Composite Bonding and Repair | p. 36 Fire Retardants | p. 45 Mold Release | p. 58 Liquid Shim | p. 46 Laminate and Wet Lay-up Resins | p. 50 Potting and Edge Fill | p. 54 Film Adhesives | 5 Structural Adhesives Film Adhesives With over four decades of experience: LOCTITE film adhesives Film adhesives: the basics Film adhesives are pre-catalyzed adhesives offered in sheet form for metal, composite bonding, and honeycomb applications. Film adhesives are offered in defined areal weights in roll or sheet form. Advanced level: LOCTITE film adhesives Our broad portfolio of film adhesives includes advanced technologies to address today and ­tomorrow’s most demanding applications. Being a long-term partner for aircraft m­ anufacturers globally, Henkel provides sustainable film adhesive solutions that enhance p ­ erformance and safety of aircraft as well as the manufacturer’s production efficiency. Why choose LOCTITE film adhesives? ›› Enables large part manufacture ›› Better toughness ›› Durable bonding ›› Bond line thickness control ›› Handling and reliability ›› Long shop life LOCTITE film adhesives: Facts at a glance LOCTITE film adhesives key features ›› Pre-catalyzed, no mixing or measuring needed ›› Usually supplied with a scrim for bond line control, toughness ›› Mix of epoxy resin and curing agent cast into a film. and handling ›› Typical thickness ranges from 5 mils to 15 mils (0.1 – 0.4 mm) ›› Allows precise placement of adhesive on part ›› Enables up to 15 days to assemble aircraft parts ›› Allows precise amount of adhesive to be placed on part ›› Controlled flow, ability to reticulate ›› Bonds various substrates Key factors to consider when choosing the right LOCTITE film adhesive: ›› Environmental and temperature resistance ›› Fracture toughness ›› Cure time and temperature ›› Lightning strike protection © Henkel. With partnership of FACC team im Ried im Innkreis, Austria. high fatigue resistance.500 psi / 3. maximum durability and significant production costs 77 °F / 25 °C) – FILM 20 Days 20 Days 15 Days savings.N / m 50 m.400 psi / 9.6 MPa 25. LOCTITE has products covering service temperatures from 250 ºF / 121 ºC to 180 °F (psi) / 4. If it does. LOCTITE EA 9258.5 MPa Elevated Temperature 250 °F / 121 °C: 250 °F / 121 °C: 350 °F / 177 °C: (psi / MPa) 2.N / m 89 m.000 psi / 13.136 MPa 11. 82 °C (MPa) 27.7 MPa 7.1 – 0.500 psi / 51. Henkel offers metal bonding films for original Mechanical Bell Peel 77 °F (lb / in) 54 lbs / in 13 lb / in construction and repair qualified to all major aerospace specifications.9 MPa @ 77 °F / 25 °C (psi / MPa) ›› Good tack and drape ›› Good reticulation Bulk Properties Tg Dry (°F / °C) 248 °F / 120 °C 240 °F / 116 °C 392 °F / 200 °C ›› Excellent adhesion to aluminum and composite substrates Tg Wet (°F / °C) 210 °F / 99 °C 200 °F / 93 °C 300 °F / 150 °C Tensile Strength (dogbone) 7.6 MPa 1.3 MPa 40.8 MPa 1.377 MPa – @ 77 °F (ksi) / 25 °C (MPa) Elongation LOCTITE metal & honeycomb bonding: @ 77 °F / 25 °C (% at break) 7.lb / 3 in 60 in.3 MPa 33.900 psi / -55 °C (MPa) 37.lb / 3 in ›› Improved toughness Peel @ 77 °F (in·lb/in) / 25° (m·N/m) 80 m.1 MPa applications.3 MPa 310 ksi / 2.100 psi / 7.0 MPa TENSILE LAP SHEAR 77 °F (psi) / 6.000 psi / 3.N / m ›› Excellent resistance to high temperatures Flatwise Tension 1. LOCTITE films are one – 25 °C (N / 25 mm) 240 N / 25 mm 58 N / 25 mm Properties component.000 psi / 6.5 % – Compressive Strength Facts at a glance @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus @ 77 °F (ksi) / 25 °C (MPa) 11.1 AERO .lb / 3 in 12 in. Materials are specifically designed for m­ aximum T Peel 77 °F (lb / in) 37 lbs / in 35 lbs / in – durability.300 psi / 9. heat curing thin film adhesives.500 psi / 51.000 psi / 5.700 psi / – 550 ºF / 288 ºC and will bond to chemically treated metallic substrates.3 MPa 310 ksi / 2.500 psi / 5.0 MPa 27.377 MPa 346 ksi / 2.0 MPa 2.5 % 7.500 psi / 79. Out-time (Days @ 10 Days 10 Days 10 Days 90 °F / 32 °C) – FILM In the honeycomb and metal assembly segment.136 MPa – – Product LOCTITE LOCTITE LOCTITE New Product Name EA 9628 EA 9628H EA 9658 LOCTITE metal and honeycomb film key features AERO AERO AERO ›› Pre-catalyzed. no mixing or measuring ›› Controlled flow Hysol® Hysol® Hysol® Known As EA 9628™ EA 9628H™ EA 9658™ ›› Typical thicknesses range from 5 mils to 15 mils (0.6 MPa 1.4 mm) ›› Ability to reticulate ›› More durable bonds ›› Long out time Availability Packaging Roll Roll Roll LOCTITE LOCTITE LOCTITE Key factors to consider when choosing the right LOCTITE product for metal & honeycomb bonding Description EA 9628 EA 9628H EA 9658 ›› Substrate preparation ›› Part size and shape AERO AERO AERO • Good Toughness • Excellent Durability • Increased toughness with high ›› Operating temperature requirements ›› Bond joint design • 250 °F/ 121 °C Cure • 250 °F/ 121 °C Cure temperature performance • Bonds Many Materials • Applications Include ­Helicopter • Designed for composite.800 psi / 19 MPa Why choose LOCTITE metal & honeycomb solutions? Honeycomb Climbing Drum 60 in.500 psi / 79.800 psi / The LOCTITE portfolio of metal bonding films is broad and addresses many needs of customer 25 °C (MPa) 41. high strength and toughness with temperature resistance designed for their o ­ perating 25 °C (N / 25 mm) 165 N / 25 mm 156 N / 25 mm environment -67 °F (psi) / 5.7 MPa – @ 77 °F (psi) / 25 °C (MPa) Tensile Modulus 345 ksi / 2.9 MPa 38. this is a LOCTITE solution. metal or ›› Operating environment ›› Strength requirements (peel or shear) • Excellent Durability Blade Bonding honeycomb • Good Toughness • State of the art flow control to • Product is preferred for helicopter minimize hole blockage and excess blade c­ onstruction because of the flash/flow product flow ­characteristics and • Thermally stable its ability to be cured in an out of • Offered with a companion low VOC autoclave process water based c­ orrosion inhibiting ­primer.850 psi / 4. Metal & Honeycomb Bonding | 7 Structural Adhesives Film AdhesivesMetal & Honeycomb Bonding Metal & Honeycomb Bonding Application Metal & Honeycomb • • • Bonding Qualified to major aerospace specifications: Characteristics 250 °F / 121 °C Service 300 °F / 149 °C Service • • LOCTITE metal & honeycomb bonding products 350 °F / 177 °C Service 550 °F / 288 °C Service • Cure Temperature (°F / °C) 250 °F / 121 °C 250 °F / 121 °C 350 °F / 177 °C Cure Time 90 Minutes 90 Minutes 60 Minutes Fully developed metal & honeycomb solutions Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) How to identify a technically advanced metal & honeycomb bonding solution? Just ask if it offers Out-time (Days @ very low weight. 3 MPa 1298 psi / 9.912 MPa – @ 77 °F (ksi) / 25 °C (MPa) Elongation – – 3.0 MPa 31.000 psi / 6.3 ksi / 1.839 psi / 47.3 MPa – @ 77 °F (psi) / 25 °C (MPa) Tensile Modulus – – 450 ksi / 3.5 Mpa 41.0 MPa 180 °F (psi) / 3.5 MPa 2.000 psi / 6.507 psi / – – 82 °C (MPa) 26.400 psi / 23.400 psi / 16.4 MPa @ 77 °F / 25 °C (psi / MPa) Bulk Properties Tg Dry (°F / °C) 568 °F / 298 °C 240 °F / 115 °C 302 °F / 150 °C 253 °F / 123 °C 293 °F / 145 °C Tg Wet (°F / °C) 410 °F / 210 °C 200 °F / 95 °C 203 °F / 95 °C 200 °F / 93 °C 190 °F / 88 °C Tensile Strength (dogbone) – – 11.6 N / 25 mm 334 N / 25 mm 89 N / 25 mm Properties T Peel 77 °F (lb / in) – – – – – 25 °C (N / 25 mm) -67 °F (psi) / 2.000 psi / 76 MPa 6.00 % – @ 77 °F / 25 °C (% at break) Compressive Strength – – – – – @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus – – – – – @ 77 °F (ksi) / 25 °C (MPa) Product LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE New Product Name EA 9673 EA 9690 EA 9695 EA 9696 EA 7000 AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9673™ (BMi) EA 9690™ EA 9695™ EA 9696™ PL 7000™ NEW! Availability Packaging Roll Roll Roll Roll Roll LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EA 9673 EA 9690 EA 9695 EA 9696 EA 7000 AERO AERO AERO AERO AERO • Service to 550 °F / 288 °C • Low Flow • X-ray Opaque • Excellent Environmental Resistance • Dual temperature cure capabilities • No Volatiles During Cure • Exceptional Peel Strength • Excellent Environmental Resistance • High Toughness ­Maintaining Ser.lb / 3in Peel @ 77 °F (in·lb/in) / – 25° (m·N/m) 80 N.4 MPa 1.N / m 116 m.4 Mpa 2.600 psi / -55 °C (MPa) 13.100 MPa 277.8 MPa 1.0 MPa 34.00 % 16. • Epoxy film adhesive for composite • Bismalimide based chemistry • Available with Knit or Non-Woven • Reticulatable vice Temperature bonding applications Mat • Good Pre and Post Bond Moisture • Balanced Flow • Excellent performance properties in • Excellent Performance with Low Resistance • Allows from composite bonding Pressure Cures • Low Flow 225 °F to 265 °F / • Excellent results on ­composite • Allows 250 °F / 121 °C or 350 °F / 107 °C to 129 °C Cure surfaces 177 °C Cure • Long Out-time Facilitates Shop • Excellent fracture ­toughness (G1c) • Co-Cure with Composites Floor Usage and Repair Applications • Long Out time Facilitates Shop • Reticulatable Floor Usage and Repair Applications .2 Mpa TENSILE LAP SHEAR 77 °F (psi) / 2.m / m 82 m.lb / 3 in 78 lbs / in 27 in.350 psi / 4.300 psi / 9.8 MPa 42.9 MPa 31.lb / in 18 in.3 MPa 31.400 psi / 7.8 MPa 43.8 Mpa 30.500 psi / 25 °C (MPa) 13.5 MPa 3.1 Mpa Elevated Temperature 350 °F / 177 °C: 250 °F / 121 °C: 300 °F / 149 °C: 250 °F / 121 °C: 270 °F / 132 °C: (psi / MPa) 2.0 MPa 1.000 psi / 4.900 psi / 4.000 psi / 12.500 psi / 4.3 MPa 26.3 MPa 48.070 psi / 7.N / m Flatwise Tension – 925 psi /6.100 psi / 14.000 psi / 6.N / m 40 m.00 – 4. Metal & Honeycomb Bonding Metal & Honeycomb Bonding | 9 Structural Adhesives Film Adhesives Metal & Honeycomb Bonding Notes Application Metal & Honeycomb • • • • • Bonding Characteristics 250 °F / 121 °C Service • • 300 °F / 149 °C Service • • 350 °F / 177 °C Service 550 °F / 288 °C Service • 350 °F / 177 °C + 250 °F / 121 °C or 225 – 275 °F / 250 °F / 121 °C or Cure Temperature (°F / °C) 250 °F / 121 °C 475 °F / 121 °C 350 °F / 177 °C 107 – 129 °C 350 °F / 177 °C Cure Time 60 Minutes / 120 Minutes 60 Minutes 60 – 120 Minutes 60 – 90 Minutes 60 – 120 Minutes Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) Out-time (Days @ 30 Days 14 Days 90 Days 60 Days 30 Days 77 °F / 25 °C) – FILM Out-time (Days @ 15 Days 10 Days 45 Days 30 Days 30 Days 90 °F / 32 °C) – FILM Mechanical Bell Peel 77 °F (lb / in) 87 lbs / in 20 lbs / in 75 lbs / in 20 lbs / in – 25 °C (N / 25 mm) 387 N / 25 mm 89.100 psi / 5.0 MPa Honeycomb Climbing Drum 18 in.000 psi / 3.200 psi / 8. 377 MPa 346 ksi / 2. let -55 °C (MPa) 37.136 MPa 310 ksi / 2.500 psi / 51.N / m 25° (m·N/m) ›› Bond line thickness control Flatwise Tension 1.0 MPa 27.1 MPa materials.000 psi / 6. manufacturers need Out-time (Days @ 10 Days 10 Days 10 Days the right adhesives to bond composite sub-components with excellent chemical resistance and 90 °F / 32 °C) – FILM extraordinary mechanical performance.5 % 7.6 MPa 1.lb / 3 in ›› Improved toughness Peel @ 77 °F (in·lb/in) / 80 m.9 MPa @ 77 °F / 25 °C (psi / MPa) ›› Good tack and drape ›› Excellent adhesion to composite substrates Bulk Properties Tg Dry (°F / °C) 248 °F / 120 °C 240 °F / 116 °C 392 °F / 200 °C Tg Wet (°F / °C) 210 °F / 99 °C 200 °F / 93 °C 300 °F / 150 °C Tensile Strength (dogbone) 7.7 MPa 7.9 MPa 38.377 MPa – Facts at a glance 7.5 MPa Why choose LOCTITE composite bonding adhesives? Elevated Temperature 250 °F / 121 °C: 250 °F / 121 °C: 350 °F / 177 °C: (psi / MPa) 2.100 psi / 7.000 psi / 3.500 psi / 51. metal or • Excellent Durability Blade Bonding honeycomb • Good Toughness • State of the art flow control to • Product is preferred for helicopter minimize hole blockage and excess blade c­ onstruction because of the flash/flow product flow ­characteristics and • Thermally stable its ability to be cured in an out of • Offered with a companion low VOC autoclave process water based ­corrosion inhibiting ­primer.3 MPa – @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus 310 ksi / 2. Composites Bonding Composites Bonding | 11 Structural Adhesives Film Adhesives Composite Bonding Application Composite • • • When structural integrity matters: Characteristics 250 °F / 121 °C Service 300 °F / 149 °C Service • • LOCTITE composite bonding 350 °F / 177 °C Service 550 °F / 288 °C Service • and repair film adhesives Cure Temperature (°F / °C) 250 °F / 121 °C 250 °F / 121 °C 350 °F / 177 °C Cure Time 90 Minutes 90 Minutes 60 Minutes Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) Concerning critical aircraft components.900 psi / create efficient structures.800 psi / 19 MPa ›› Good environmental resistance Honeycomb Climbing Drum 60 in.500 psi / 79.500 psi / 5.N / m 89 m.8 MPa 1.N / m 50 m.136 MPa – @ 77 °F (ksi) / 25 °C (MPa) LOCTITE composite bonding adhesives key features: Product LOCTITE LOCTITE LOCTITE ›› High temperature service ›› Toughness tailorable to requirements New Product Name EA 9628 EA 9628H EA 9658 AERO AERO AERO ›› Compatibility with aerospace prepreg systems ›› Variations in form: thickness or weight Hysol® Hysol® Hysol® Known As ›› Good wetting of composite surfaces ›› Excellent chemical resistance EA 9628™ EA 9628H™ EA 9658™ ›› High mechanical performance Availability Packaging Roll Roll Roll Key factors to consider when choosing the right LOCTITE composite bonding adhesive LOCTITE LOCTITE LOCTITE Description EA 9628 EA 9628H EA 9658 ›› Service temperature ›› Glass transition temperature (Tg) AERO AERO AERO • Good Toughness • Excellent Durability • Increased toughness with high ›› Shelf life / out-time ›› Toughness • 250 °F/ 121 °C Cure • 250 °F/ 121 °C Cure temperature performance ›› Cure temperature • Bonds Many Materials • Applications Include H ­ elicopter • Designed for composite.000 psi / 13.0 MPa TENSILE LAP SHEAR you take advantage of stiffness properties of composites and provide a separation of dissimilar 77 °F (psi) / 6.7 MPa – @ 77 °F (psi) / 25 °C (MPa) Tensile Modulus LOCTITE composite bonding adhesives: @ 77 °F (ksi) / 25 °C (MPa) Elongation 345 ksi / 2. LOCTITE EA 9258. 180 °F (psi) / 4.lb / 3 in 60 in.6 MPa 25.5 % – @ 77 °F / 25 °C (% at break) Compressive Strength 11.500 psi / 79. some questions might come up Out-time (Days @ 20 Days 20 Days 15 Days 77 °F / 25 °C) – FILM In order to preserve the structural integrity of critical aircraft components.6 MPa 1.000 psi / 5.400 psi / 9.3 MPa 33. No fasteners are needed.lb / 3 in 12 in.800 psi / 25 °C (MPa) 41. Bell Peel 77 °F (lb / in) 54 lbs / in 13 lb / in Mechanical – 25 °C (N / 25 mm) 240 N / 25 mm 58 N / 25 mm Properties Henkel gives a strong answer: LOCTITE composite bonding adhesives T Peel 77 °F (lb / in) 37 lbs / in 35 lbs / in – 25 °C (N / 25 mm) 165 N / 25 mm 156 N / 25 mm LOCTITE products for composite bonding fulfill all these requirements and allow engineers to -67 °F (psi) / 5.3 MPa 11.300 psi / 9.500 psi / 3. They offer lower adherent thickness.0 MPa 2.700 psi / – 82 °C (MPa) 27.850 psi / 4.3 MPa 40.1 AERO . N / m Flatwise Tension – 925 psi /6.600 psi / -55 °C (MPa) 13.lb / 3 in 78 lbs / in 27 in.912 MPa – @ 77 °F (ksi) / 25 °C (MPa) Elongation – – 3.00 – 4.100 psi / 14.000 psi / 3.500 psi / 25 °C (MPa) 13.0 MPa 1.4 MPa @ 77 °F / 25 °C (psi / MPa) Bulk Properties Tg Dry (°F / °C) 568 °F / 298 °C 240 °F / 115 °C 302 °F / 150 °C 253 °F / 123 °C 293 °F / 145 °C Tg Wet (°F / °C) 410 °F / 210 °C 200 °F / 95 °C 203 °F / 95 °C 200 °F / 93 °C 190 °F / 88 °C Tensile Strength (dogbone) – – 11.3 MPa 1298 psi / 9.N / m 40 m. Composites Bonding Composites Bonding | 13 Film Adhesives Structural Adhesives Film Adhesives Film Adhesives Composite Bonding Notes Application Composite • • • • • Characteristics 250 °F / 121 °C Service • • 300 °F / 149 °C Service • • 350 °F / 177 °C Service 550 °F / 288 °C Service • 350 °F / 177 °C + 250 °F / 121 °C or 225 – 275 °F / 250 °F / 121 °C or Cure Temperature (°F / °C) 250 °F / 121 °C 475 °F / 121 °C 350 °F / 177 °C 107 – 129 °C 350 °F / 177 °C Cure Time 60 Minutes / 120 Minutes 60 Minutes 60 – 120 Minutes 60 – 90 Minutes 60 – 120 Minutes Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) Out-time (Days @ 30 Days 14 Days 90 Days 60 Days 30 Days 77 °F / 25 °C) – FILM Out-time (Days @ 15 Days 10 Days 45 Days 30 Days 30 Days 90 °F / 32 °C) – FILM Mechanical Bell Peel 77 °F (lb / in) 87 lbs / in 20 lbs / in 75 lbs / in 20 lbs / in – 25 °C (N / 25 mm) 387 N / 25 mm 89.0 MPa 31.900 psi / 4.8 MPa 43.100 psi / 5.000 psi / 76 MPa 6.m / m 82 m.000 psi / 6.000 psi / 12.00 % 16.8 Mpa 30.000 psi / 6.507 psi / – – 82 °C (MPa) 26.200 psi / 8.400 psi / 7.2 Mpa TENSILE LAP SHEAR 77 °F (psi) / 2.500 psi / 4.8 MPa 42.9 MPa 31. • Epoxy film adhesive for composite • Bismalimide based chemistry • Available with Knit or Non-Woven • Reticulatable vice Temperature bonding applications Mat • Good Pre and Post Bond Moisture • Balanced Flow • Excellent performance properties in • Excellent Performance with Low Resistance • Allows from composite bonding Pressure Cures • Low Flow 225 °F to 265 °F / • Excellent results on ­composite • Allows 250 °F / 121 °C or 350 °F / 107 °C to 129 °C Cure surfaces 177 °C Cure • Long Out-time Facilitates Shop • Excellent fracture ­toughness (G1c) • Co-Cure with Composites Floor Usage and Repair Applications • Long Out time Facilitates Shop • Reticulatable Floor Usage and Repair Applications .lb / in 18 in.N / m 116 m.3 MPa – @ 77 °F (psi) / 25 °C (MPa) Tensile Modulus – – 450 ksi / 3.300 psi / 9.0 MPa 180 °F (psi) / 3.4 MPa 1.000 psi / 6.8 MPa 1.5 Mpa 41.4 Mpa 2.6 N / 25 mm 334 N / 25 mm 89 N / 25 mm Properties T Peel 77 °F (lb / in) – – – – – 25 °C (N / 25 mm) -67 °F (psi) / 2.lb / 3in Peel @ 77 °F (in·lb/in) / – 25° (m·N/m) 80 N.00 % – @ 77 °F / 25 °C (% at break) Compressive Strength – – – – – @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus – – – – – @ 77 °F (ksi) / 25 °C (MPa) Product LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE New Product Name EA 9673 EA 9690 EA 9695 EA 9696 EA 7000 AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9673™ (BMi) EA 9690™ EA 9695™ EA 9696™ PL 7000™ NEW! Availability Packaging Roll Roll Roll Roll Roll LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EA 9673 EA 9690 EA 9695 EA 9696 EA 7000 AERO AERO AERO AERO AERO • Service to 550 °F / 288 °C • Low Flow • X-ray Opaque • Excellent Environmental Resistance • Dual temperature cure capabilities • No Volatiles During Cure • Exceptional Peel Strength • Excellent Environmental Resistance • High Toughness ­Maintaining Ser.5 MPa 2.839 psi / 47.070 psi / 7.000 psi / 4.400 psi / 16.400 psi / 23.3 MPa 48.5 MPa 3.350 psi / 4.0 MPa Honeycomb Climbing Drum 18 in.3 MPa 26.3 ksi / 1.1 Mpa Elevated Temperature 350 °F / 177 °C: 250 °F / 121 °C: 300 °F / 149 °C: 250 °F / 121 °C: 270 °F / 132 °C: (psi / MPa) 2.0 MPa 34.100 MPa 277.3 MPa 31. (Days @ 90 °F / 32 °C) 10 Days 10 Days – FILM LOCTITE peel plies: The ideal method to save time and costs Bulk Properties Tg Dry (°F / °C) 270 °F / 132 °C 228 °F / 109 °C Henkel’s peel ply enables process efficiency by minimizing surface preparation. Product LOCTITE LOCTITE New Product Name EA 9896 WPP EA 9895 WPP Why choose LOCTITE peel plies? AERO AERO ›› Ease of removal Hysol® Hysol® Known As EA 9896 WPP™ NEW! EA 9895 WPP™ ›› Minimal residual polyester fibers on substrate after removal ›› Thin residual resin layer Availability Packaging Roll Roll ›› Controlled failure / release path LOCTITE LOCTITE Description ›› Optimized interfacial strength EA 9896 WPP EA 9895 WPP AERO AERO ›› Promotes cohesive failure modes within the bondline • Durable bond • Provides: More durable bond than dry peel ply fabrics • Minimal residual nylon fibers left on substrate • Minimal residual polyester fibers left on substrate ›› Generate more durable bonding surface than dry fabric after removal after removal • Minimal risk of interfacial failure in bonded structures • Promotes cohesive failure mode • No sanding or solvent wiping required for bonding • Compatible with third generation composites • Minimal force required to remove peel ply layer • No sanding or solvent wiping required for bonding • Minimal force required to remove peel ply layer LOCTITE peel plies: Facts at a glance Notes LOCTITE peel plies key features ›› Compatible with third generation composites ›› Protective layer ›› No sanding or solvent wiping required of bonding surface ›› Good shop life ›› Minimal force required to remove peel ply layer Key factors to consider when choosing the right LOCTITE peel ply ›› Polyester vs. – FILM peel ply is the most commonly recommended process because it creates a more uniform surface Out-time preparation than hand or machine abrasion. It ensures a consistent bonding surface. Out-time (Days @ 77 °F / 25 °C) 14 Days 14 Days bon fiber composite: Surface abrasion. i. nylon peel ply ›› Compatibility with composite prepreg resin ›› Cure temperature ›› Dry or wet peel ply . peel ply.e. Composite Surface Preparation Composite Surface Preparation | 15 Structural Adhesives Film Adhesives Composite Surface Preparation Application Peel Ply • • Clean and cost efficient surface preparation: Characteristics 250 °F / 121 °C Service • 300 °F / 149 °C Service • With LOCTITE peel plies Cure Temperature (°F / °C) 250 °F / 121 °C 350 °F / 177 °C Cure Time 90 – 120 Minutes 90 – 120 Minutes Peel ply: The ideal preparation method for treating surfaces evenly Storage Temperature (°F / °C) 0 °F / -18 °C 0 °F / -18 °C There are two primary methods for adhesive bond preparation of the surface of a pre-cured car. LOCTITE peel ply provides part longevity and reduces maintenance costs. Of the two. Tg Wet (°F / °C) 217 °F / 103 °C – with a high quality bond with tough state-of-the-art composites. and the use of release ply fabric. 1™ BLK HC 9837.6 MPa 20.990 psi – – – – 25 °C (MPa) 20. Description EA 9837. The product paintable surface. Configuration. paintable surface. A lightweight solution is important too. Economically. is manufactured ›› Excellent retention of hardness after fluid soak ›› Resistance to high thermal fatigue situations Available in One.1 EA 9837. ›› Process labor reduction sand and fill operations ›› Easy repair after lightning strike ›› Inventory reduction from two raw materials to one . Surfacing Film & Lightning Strike Protection Surfacing Film & Lightning Strike Protection | 17 Structural Adhesives Film Adhesives Surfacing Film & Lightning Strike Characteristics 350 °F / 177 °C Service • • • • • • Cure Temperature 250 °F / 121 °C or 251 °F / 121 °C 252 °F / 121 °C 252 °F / 121 °C or 250 °F / 121 °C or 251 °F / 121 °C or (°F / °C) 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C Boosting surface quality: Cure Time 60 Minutes 60 Minutes 60 Minutes 60 – 120 Minutes 60 – 120 Minutes 60 – 120 Minutes LOCTITE surfacing films for Storage Temperature (°F / °C) 0 °F -18 °C 0 °F -18 °C 0 °F -18 °C 0 °F -18 °C 0 °F -18 °C 0 °F -18 °C lightning strike protection Out-time (Days @ 90 Days 90 Days 90 Days 45 Days 45 Days 45 Days 77 °F / 25 °C) – FILM Out-time (Days @ 21 Days 21 Days 21 Days 10 Days 10 Days 10 Days 90 °F / 32 °C) – FILM Mechanical -67 °F (psi) / – – – – – – -55 °C (MPa) How to benefit from the right surfacing film solution Properties TENSILE LAP SHEAR 77 °F (psi) / 2. they offer up to 30 % weight savings compared to existing surfacing films – and they lower the composite Availability Packaging Roll Roll.1™ LSC EA 9845 SF™ EA 9845 LSC™ EA 9845 LSA™ With our LOCTITE portfolio. lightning strike porosity. Technically. with a non-woven Side-Tacky (OST) Side-Tacky (OST) fabric for support. containing copper surfacing film surfacing film surfacing film comparable with compatible with screen designed to designed to containing copper containing ›› Maximum protection against lightning strikes ›› Out-of-autoclave capable lightning strike lightening strike lightening strike improve the screen designed aluminum screen foils.1 LS EA 9845 EA 9845 LC EA 9845 LA How to gain even more benefits: AERO AERO AERO AERO AERO AERO LOCTITE surfacing films & lightning strike protection Known As SynSkin® SynSkin® SynSkin® Hysol® Hysol® Hysol® HC 9837. Configuration.1 BLK EA 9837.1 EA 9837. But this is not all: laminated films composed of a surfacing film and a conductive metal Elevated Temperature foil protect the composite structure from damage caused by lightning strikes. Sheet Roll – – part finishing costs. surface quality to lightning strike designed to ›› Reduce core mark-through ›› No microcracking core crush and core crush and of honeycomb protection. It stiffened composite protection.6 MPa Surfacing films are designed to improve the surface quality of honeycomb stiffened composite parts. minimizes protection. high quality paintable surfaces and a maximum of LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE product & shop flexibility.1 BLK EA 9837.990 psi 2. Available in One. tack properties. decrease surface preparation time and provide protection of 180 °F (psi) / – – – – – – 82 °C (MPa) structural fibers. They also provide a barrier for dissimilar materials. they provide durable. you can be sure to get the technically most advanced solution.1 LS EA 9845 EA 9845 LC EA 9845 LA AERO AERO AERO AERO AERO AERO Why choose LOCTITE surfacing films & lightning strike protection? is an epoxy based is an epoxy based is an epoxy based is an epoxy-based is an epoxy-based is an epoxy-based film with good film with good composite film composite composite composite ›› Minimize core crush ›› Increased UV and paint stripper resistance tack properties. And process 109 °C 109 °C 109 °C 105 °C 105 °C 105 °C ­efficiency should be maximized – including easy repair after lightning strike. (psi / MPa) – – – – – – Protect your aircraft from lightning strike damage Bulk Properties Tg Dry (°F / °C) 273 °F 274 °F 275 °F 254 °F 252 °F 253 °F 134 °C 134 °C 134 °C 122 °C 122 °C 122 °C What are the requirements for optimum lightning strike protection of aircraft composite parts? A 228 °F 229 °F 230 °F 223 °F 221 °F 222 °F Tg Wet (°F / °C) ­maximum electrical conductivity is essential.1™ HC 9837. LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9837. LOCTITE surfacing films & lightning strike protections: Facts at a glance Notes LOCTITE surfacing films key features: ›› High surface quality: Low flow ›› Reduce surface imperfections ›› Good paint adhesion without sanding ›› Minimize pre-paint preparation ›› Available in lightning strike configurations LOCTITE lightning strike protection key features: ›› Easier handling than stand-alone expanded foil during lay-up. Sheet Roll. It offers porosity. ›› Protect the composites ›› High quality paintable surfaces high quality offers high quality parts. minimizes foils. low density ›› Attach and bond to core walls ›› User-friendly processing Microspheres Thermosetting resin matrix LOCTITE syntactic core sandwich construction LOCTITE syntactic core machined shape . improving productivity. high impact resistance. They ›› Service temperature ›› Process conditions offer excellent slump resistance and exothermic properties. Syntactic. They provide a rub strip for jet engine compressor blades combining high erosion resistance with low abrasion at low density. load transfer and easier formability? With LOCTITE structural syntactic materials. deep core filling or co-cure conditions – and are easier to insert into core gaps. Materials are available for OEM installation and for repair and maintenance to ensure the fleet is always operational. high the right LOCTTITE core fill and core splice materials panel strength – and. LOCTITE materials expand during heat cure up to 2 – 3 times their original size. the right LOCTITE abradable materials ›› Abrasion resistance required ›› Density As foaming films. minimum gauge stiffened panels. core fill and abradable materials? ›› Improved mechanical strength. toughness and ›› Sag resistant LOCTITE syntactic core energy absorption ›› Qualified by major OEMs ›› Uniform expansion ›› Panel thickness can be contoured. ›› Cure Time ›› Mechanical properties LOCTITE core splice and expanding materials meet your needs ›› Service Temperature ›› Process conditions Our high performance core splices are used to obtain a uniform load transfer from one section of core to ­another before being bonded on the assembly line. Henkel provides the right choice for structural and low d ­ ensity sandwich panels. This Abradable materials: Key facts to consider when choosing process also serves as a method of preventing moisture ingression in honeycomb-stiffened parts through the core splice joint. Core Fill and Abradable LOCTITE Syntactic. an optimum stiffness to weight. being ideal for thick splices. They offer maximum structural performance. ›› Toughness ›› Repair Materials for improved abrasion resistance Henkel’s abradable materials ensure that today’s aircraft engines can operate at maximum efficiency. of course. They enable filling the gap up to the skin surface. core filling. Why choose LOCTITE syntactics. Applications include low density panel stiffening. and Expanding materials: Key factors to consider when choosing ­sandwich panel edge build-up. The products are non-expanding films ›› Cure Temperature ›› Density supplied in a range of thicknesses. local build-ups ›› Enable load transfer can be included Composite LOCTITE expanding syntactic film ›› Enable thick and complex sandwich ­structures ›› Abrasion & erosion resistance laminate ›› No mark-off due to bonding or honeycomb ›› Expanding. Core Fill and Abradable: Light weight. splicing and the right LOCTITE structural syntactic materials abrasion resistance ›› Service temperature ›› Compression strength ›› Process temperature ›› Core thickness required ›› Application ›› Expanding or non-expanding Want to have optimum stiffness. Core Fill and Abradable | 19 Structural Adhesives Syntactic. high stiffness and optimum load transfer: Facts at a glance LOCTITE syntactic materials for structural Syntactic Materials: Key factors to consider when choosing sandwich panel. LOCTITE LOCTITE LOCTITE LOCTITE Description EF 9899 EF 9899CF EF 9890 EF 557 AERO AERO AERO AERO is a 250 °F / 121 °C or is a medium density low is an expanding ­modified is a modified epoxy ­foaming 350 °F / 177 °C curing ­exotherm expanding epoxy film that cures at adhesive that may be ­expanding syntactic film.800 psi / 150 MPa @ 73 °F (psi) / 23 °C (MPa) Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) Tensile Strength 4.2 MPa 35 pcf: SynCore® SynCore® SynCore® Known As 6. edge close core fill. The low ­Additional features include materials.45 @ 0.1 HC 9875 Block Compressive (dry) 500 @ 12 pcf density 26 pcf: – – AERO AERO AERO @ 77 °F (psi) / 25 °C (MPa) 3. Modified core material. Excellent is a structural syntactic film.800 psi / 61 MPa 21.600 psi / 11.3 MPa 5.700 psi / 32 MPa 4.800 psi / 33 MPa 5.500 psi / 44.6 MPa – 77 °F / 25 °C) – FILM @ 77 °F (psi) / 25 °C (MPa) Out-time (Days @ Tensile Modulus 10 Days 10 Days 10 Days – – 62ksi / 430 MPa – 90 °F / 32 °C) – FILM @ 77 °F (ksi) / 25 °C (MPa) Compressive Strength Bulk Properties Tensile Strength (dogbone) 1. . Core Fill Film and Abradable Adhesives | 21 Structural Adhesives Syntactic. or reinforce honeycomb homogenous cell (0.100 psi / 7.500 psi / 17. Sheet Roll. Lightweight syntactic Availability Packaging Roll. Co-curable 121 °C prepegs.1 HC 9875 9899™ 9899CF™* MA 557™ AERO AERO AERO Abradable Seal is a structural syntactic film.700 psi / 32 MPa 4.425 psi / 37.366 MPa 85 ksi /585 MPa – 380 ksi / 2.800 psi / 150 MPa @ 77 °F (psi) / 25 °C (MPa) @ 77 °F (psi) / 25 °C (MPa) 19 pcf: Products LOCTITE LOCTITE LOCTITE 1.800 psi / 61 MPa 21. High ­compressive out. Modified ­syntactic core material. Co-curable with 250 °F / ­epoxy.5 MPa 77 °F (psi) / 25 °C (MPa) Cure Time 60 Minutes 60 Minutes 120 Minutes Properties Tube Shears @ Storage Temperature – – – 1.2 ksi / 1. Its applications exotherm chemistry makes areal weight and width.000 psi / 34.3 Mpa 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 250 °F(psi) / 121 °C (MPa) (°F / °C) Storage Time > 12 Months > 12 Months > 12 Months Bulk Properties Tg Dry (°F / °C) 383 °F / 195 °C 380 °F / 193 °C – – Out-time (Days @ Tensile Strength (dogbone) 15 Days 15 Days 15 Days – – 1. Co-curable with 350 °F / high compressive loading.758 MPa 580 ksi / 4. Lightweight crush strength. include h ­ oneycomb core this product ideal for deep ­stabilization. ­syntactic film suitable for 250 °F / 121 °C.1 HC 9872. Sheet Roll.440 psi / 10.300 psi / 9. Designed to witstand ­epoxy.1™ 9875™ Product LOCTITE LOCTITE LOCTITE LOCTITE Availability Packaging Roll. It is closed cell process. with 350 °F / 177 °C prepegs.606 MPa 400 ksi / 2. Syntactic. RTM core.000 MPa @ 73 °F (psi) / 23 °C (MPa) Out-time (Days @ 10 Days 10 Days 10 Days 5 Days 90 °F / 32 °C) – FILM Process & Cure Temperature (°F / °C) 250 °F / 121 °C 350 °F / 177 °C 350 °F / 177 °C Handling Mechanical Tube Shears @ – 1.000 psi / 62 MPa 8. Sheet ­syntactic core material. Its typical cured density which require high abrasion designed to seal.4 MPa 1. splice. ­Commonly cured at 250 °F / 121 °C It expands using a unique core filling ­applications.758 MPa 580 ksi / 4.5 MPa @ 73 °F (psi) / 23 °C (MPa) Out-time (Days @ 15 Days 15 Days 15 Days 10 Days 77 °F / 25 °C) – FILM Tensile Modulus 380 ksi / 2.56 g/cc).000 MPa @ 77 °F (ksi) / 25 °C (MPa) @ 77 °F (ksi) / 25 °C (MPa) Flexural Strength Block Compressive (dry) – – 1.0 MPa – 9. Excellent is a structural syntactic film.063 psi / 7.8 Mpa 9823.606 MPa 400 ksi / 2.9 MPa New Product Name HC 9823. Core Fill and Abradable Structural Syntactic Materials: Non Expanding Core Fill & Abradable Application Syntactic Film • • • Application Abradable Seal • Non-Expandanding Core Splice / Filler • • • Syntactic Film Expanding 180 °F / 82 °C Service Characteristics 250 °F / 121 °C Service • • • 300 °F / 149 °C Service • 250 °F / 121 °C Service • 300 °F / 149 °C Service • • 350 °F / 177 °C Service 300 °F / 149 °C Service 550 °F / 288 °C Service • – High Strength Cure Temperature 250 – 350 °F / 250 – 350 °F / 250 – 350 °F / 250 °F / 121 °C (°F / °C) 121 – 177 °C 121 – 177 °C 121 – 177 °C Product Continuous Service Maximum Maximum Maximum Temperature (F° / C°) 250 °F / 121 °C 350 °F / 177 °C 350 °F / 177 °C Characteristics Cure Time 60 Minutes 60 Minutes 120 Minutes 60 Minutes Block Compressive (dry) 9.1™ 9872.19 g / cc 2. High moisture resistance. or 350 °F / 177 °C.500 psi / 10.000 psi / 62 MPa 8. 177 °C prepegs. providing for a ­completely range is 18 – 35 pcf and corrosion resistance.1 HC 9872. Sheet Roll New Product Name EF 9899 EF 9899CF EF 9890 EF 557 AERO AERO AERO AERO LOCTITE LOCTITE LOCTITE SynSpand® Description Known As SynSpand® SynSpand® EA 9890™ Hysol® HC 9823.5 MPa @ 77 °F (psi) / 25 °C (MPa) @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus Tensile Modulus 86 ksi / 585 MPa 198.0 MPa – 4. Lightweight moisture resistance. ­potential for some ­structural applications.0 MPa – 940 psi / 6.000 psi / 6. Sheet Roll Roll. ­structure. and many strength ­provides the others. used for ­abradable seals.800 psi / 33 MPa 5.29 – 0.000 psi / 34. . The adhesive or 350 °F / 177 °C and for service temperatures use up to 450 °F / 230 °C.7 MPa @ 77 °F (psi) / 25 °C (MPa) Block Compressive (dry) 4615 psi / 31. epoxy and may be cured at 300 °F / 149 °C.5 MPa 1.551 MPa 180 ksi / 1.150 psi / 8.2 MPa 1.682 psi / 11.190 psi / 8. Commonly 300 °F /149 °C. which may be post cure. used for abradable seals.8 MPa 2. Sheet Sheet LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EF 9835 EF 9840 EF 562SFR EA 460 AERO EF 560 AERO EF 562 AERO EF 9833.000 psi / 6. It may 250 °F / 121 °C or 350 °F / foaming core splice epoxy film that is supplied epoxy film that is supplied adhesive. Core Fill and Abradable | 23 Structural Adhesives Syntactic. cured at 250 °F /121 °C or 350 °F /177 °C. Sheet Roll Sheet Dual Cartridge Sheet Roll.241 MPa – – – – – @ 77 °F (ksi) / 25 °C (MPa) Compressive Strength – – – – – – – @ 77 °F (psi) / 25 °C (MPa) Compressive Modulus 250 ksi / 1. Commonly offers the ­advantages of 121 °C to 350 °F / 177 °C. expanding.9 MPa 77 °F (psi) / 25 °C (MPa) Properties Tube Shears @ – – 1.000 psi / 6.8 MPa – – – – – @ 77 °F (psi) / 25 °C (MPa) Product LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE New Product Name EF 9835 EF 9840 EF 562SFR EA 460 EF 560 EF 562 EF 9833.300 psi / 15.5 MPa – – – – – @ 77 °F (psi) / 25 °C (MPa) Tensile Modulus 370 ksi / 2. It is designed for as a continuous film of as a continuous film of supplied as a film for core cartridges. a fire ­retardant structural by an elevated temperature which require high erosion which require high abrasion ­adhesive.400 psi / 16.1 AERO AERO AERO AERO AERO AERO AERO SynSpand® SynSpand® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9835™ EA 9840™ EA 9833.000 psi / 6.0 MPa 1.150 psi / 8.8 MPa 1. controlled areal weight and controlled areal weight and splicing and closeout of expands and cures at is designed for service at from -67 °F / -55 °C to This product handles like an width. -55 °C to 350 °F / 177 °C.170 psi / 8. It may be cured at width.1 AERO AERO AERO AERO is a foaming epoxy ­adhesive is a low density. It is designed ­adhesive.6 MPa 1. and corrosion resistance. It may be cured at ­honeycomb panels.1™ MA 562SFR™ PL 460™ MA 560™ MA 562™ Abradable Seal Abradable Seal (BMi) Availability Packaging Roll. Core Fill and Abradable Core Fill & Abradable Notes Application Abradable Seal • • Core Splice / Filler • • • • • Characteristics 250 °F / 121 °C Service 300 °F / 149 °C Service • • 350 °F / 177 °C Service • • • • 550 °F / 288 °C Service • Cure Temperature 250 °F / 121 °C 250 °F / 121 °C 250 °F / 121 °C 250 °F / 121 °C 350 °F / 177 °C + 300 °F / 149 °C 300 °F / 149 °C (°F / °C) 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C 350 °F / 177 °C 475 °F / 121 °C" Cure Time 90 Minutes 90 Minutes 90 Minutes / 60 Minutes 90 Minutes / 60 Minutes 60 Minutes / 60 Minutes 60 Minutes 60 Minutes / 120 Minutes Storage Temperature 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C 0 °F / -18 °C (°F / °C) Out-time (Days @ 15 Days 15 Days 10 Days 30 Days 30 Days 20 Days 30 Days 77 °F / 25 °C) – FILM Out-time (Days @ 10 Days 10 Days 10 Days 10 Days 10 Days 10 Days 10 Days 90 °F / 32 °C) – FILM Mechanical Tube Shears @ – – 850 psi / 5. is a general purpose is a modified ­bismaleimide is an expanding modified is an expanding modified is an expanding foam in paste form for easy epoxy film adhesive. resistance.9 MPa 250 °F(psi) / 121 °C (MPa) Bulk Properties Tg Dry (°F / °C) – 200 °F / 93 °C – 266 °F / 130 °C – 300 °F / 149 °C 550 °F / 288 °C Tensile Strength (dogbone) – 2. It ­temperatures from 250 °F / ­temperatures from -67 °F / 350 °F / 177 °C. Syntactic. 350 °F / 177 °C followed used for abradable seals.724 MPa 144 ksi / 993 MPa – – – – – @ 77 °F (ksi) / 25 °C (MPa) Flexural Strength – – – – – – 827 psi / 5.1 Mpa 940 psi / 6.0 MPa 1.9 MPa 1. which is extrusion through packaged be cured at 250 °F / 121 °C 177 °C film. offer at least twice the improvement a room temperature drying to be in peel strength toughness over ready for bonding.3 mildry film 1. Since it is a it furnishes excellent resistance to 177 °C service.800 psi / 25 °C (MPa) 6.060 unsupported.12 mils: 13 lb / in 58 N / 25 mm Properties Bell Peel 77 °F (lb / in) 0. It is especially current 350 °F / 177 °C service film ­well-suited for use with room adhesives.1 ›› Excellent storage and out time stability ›› Adhesion to different substrates ›› Primer reactivation not required for second-stage bonding ›› Chemical resistance Availability Packaging Gallon Gallon Gallon ›› Product safety of reactive hotmelts LOCTITE LOCTITE LOCTITE Description EA 9203 EA 2000 EA 9258. It is applied with current ­temperature curing paste adhesives.1 ›› Spray of brush applications AERO AERO AERO ›› Improves production rates ›› Temperature resistance Hysol® Hysol® Hysol® Known As EA 9203™ AL 2000™ EA 9258. When cured.800 psi / 19 MPa (psi / MPa) @ 250 °F /121°C @ 380 °F / 177 °C Created for a broad application range. they are available in ozone-safe (non-CFC).3 m2 / liter / 0.24 mils: 15 lb / in – – 25 °C (N / 25 mm) 65 N / 25 mm Once a surface has been etched.900 psi / TENSILE LAP SHEAR – ready to be bonded.200 psi / 4. . Peel @ 77 °F (in·lb / in) / – 25 °(m·N / m) 17. The oxide layer from the cleaning and etching process is sensitive to decay. The etched metal surface is “active” and -67 °F (psi) / 3. Primers | 25 Structural Adhesives Primers Primers Corrosion Protection / Enhanced Bondability / Application Enhanced Bondability Enhanced Bondability Enhanced Bondability Corrosion Protection Characteristics High-end protection for sensitive surfaces: 180 °F / 82 °C Service • 350 °F / 177 °C Service • • LOCTITE primers Form 1 Part 1 Part 1 Part Mechanical 0.165 psi / 3. Flatwise Tension – – 1000 psi / 7 MPa @ 77 °F / 25 °C (psi / MPa) Why choose LOCTITE primers? PRIMER COVERAGE Square Foot / Gal @ ›› Enhance adhesion ›› Eliminate cobwebbing 0.1 AERO AERO AERO is an adhesive bonding primer is a heat curing nitrile / phenolic is a water-borned chromated which enhances adhesion on poorly water based primer.39 mils: 14 lb / in 62 N / 25 mm One of the main reasons for priming is to prevent corrosion of the part. and allows you to store metal for later use.200 SF / Gal / Mil ­thickness / Square ›› Excellent resistance to chemicals ›› Corrosion protection Meter / Liter @ 8μm 39 m2 / liter / 0. provide corrosion Honeycomb Climbing Drum 80 in·lb / in 12 in·lb / in protection and improve bond joint long term durability. it needs protection 0. It may be cured 45 – 60 ­minutes 350 °F / 177 °C) for optimum ­performance.7 m2 / liter / 0. and provides low VOCs of 142 g/liter.0254 mm 29.9 MPa 29 MPa 33 MPa LOCTITE primers care and protect perfectly Elevated Temperature – 1500psi /10 MPa 2. 77 °F (psi) / 1. It is designed to ­non-curing primer.600 SF / Gal / Mil 600 SF / Gal / Mil 1.0254 mm dry film thickness Handling Cure Temperature (°F / °C) 77 °F / 23 °C 315 °F / 157 °C 350 °F / 177 °C Cure Time – 90 Minutes 45 – 60 Minutes LOCTITE primers: Storage Temperature (°F / °C) 77 °F / 25 °C 40 °F / 5 °C 40 °F / 5 °C Facts at a glance Out-time (Days @ 77 °F / 25 °C) – FILM 365 Days 90 Days 30 Days Out-time (Days @ 366 Days 30 Days 20 Days 90 °F / 32 °C) – FILM LOCTITE primers key features Key factors to consider when choosing the right Product LOCTITE LOCTITE LOCTITE LOCTITE primer New Product Name EA 9203 EA 2000 EA 9258. it requires only chemicals and water.6 m·N / m 50 m·N / m solvent-based and solvent-free formulations.10 NWG AERO and LOCTITE EA 9658 AERO 0.0254 mm 14. aerospace primer spray equipment. LOCTITE primers are designed to promote adhesion.000 psi / 4. ­adhesive bonding primer for 350 °F / ­prepared surfaces. The data c­ ontained herin were obtained with the ­companion film adhesive LOCTITE EA 9658 0. And of course. Priming protects -55 °C (MPa) 22 MPa 27 MPa and preserves the oxide. With partnership of FACC team im Ried im Innkreis. fairing and repair. Why choose for LOCTITE paste adhesives? ›› Improve microcrack resistance ›› Reduce costs ›› Bond numerous substrates ›› Reduce weight in structural assemblies ›› Excellent thin substrates bonding ›› Provide design flexibility LOCTITE paste adhesives: Facts at a glance LOCTITE paste adhesives key features: ›› Allow use of two different materials ›› Absorb vibration ›› Distribute stresses in joints ›› Oil and fuel resistant ›› Flexible to cure temperature ›› Co-bond and co-cure Key factors to consider when choosing the right LOCTITE paste adhesive ›› Size and shape of part to be bonded ›› Process related requirements ›› Production rates and quantities © Henkel. Outperforming portfolio: LOCTITE paste adhesives As a leader in toughened paste and film adhesives. Henkel’s aerospace group offers a complete line of pre-measured packages for paste adhesives ranging from a pudding cup to a two-part cartridge kit with static mixers.and two-part epoxy paste adhesive systems for potting. Henkel provides exactly the paste adhesive solutions you need: one. bonding. titanium and composites either in rib-stiffened designs or in honeycomb designs. . Paste Adhesives | 27 Structural Adhesives Paste Adhesives Superior bonding performance: LOCTITE paste adhesives Paste adhesives: Keeping it all together Paste adhesives are structural adhesives used to bond aluminum. Austria. In other words. stainless steel. 0 MPa 8. LOCTITE products allow you to bond 82°C (Mpa) 15. Honeycomb Bonding & Repair Metal. chemical resistance and resists creep under Mechanical Bell Peel 77°F (lb / in) 35 lbs / in 35 lbs / in 6 lbs / in sustained loads.7 MPa TENSILE LAP SHEAR We combine it with efficiency: LOCTITE metal bond and repair 77°F (psi) / 5. Gallon Kit.900 psi / 1.280 psi / 64. 25°C (N / 25 mm) Properties 150 N / 25 mm 150 N / 25 mm 25 N / 25 mm Too many requirements? Not for us. -67°F (psi) / 4. Honeycomb Bonding & Repair | 29 Structural Adhesives Paste Adhesives Metal.4 MPa 600 psi / 4.000 psi / 55. It has no metallic fillers.960 MPa 375 ksi / 2. Quart Kit ›› Service temperature ›› High temperature resistance LOCTITE LOCTITE LOCTITE ›› Consistency and viscosity ›› Flexibility or toughness Description EA 9320NA EA 9321 EA 9323 AERO AERO AERO is a two-component paste adhesive is a two-component thixotropic paste is a two-component paste adhesive. .826 MPa 284 ksi / 1.8 MPa 20. Tg Wet (°F / °C) – 190 °F / 88 °C 157 °F / 69 °C Why choose LOCTITE structural metal bond paste? Tensile Strength 5. Metal.000 psi / 25°C (Mpa) 34.1 MPa 9.58 Gpa ›› Easy to apply @ 77°F (ksi) / 25°C (MPa) ›› Ready-to-use packaging solutions ›› One or two component systems Elongation 9.0 MPa 3.000 psi / 4. Elevated Temperature – 500 psi / 3.000 psi / 3.100 psi / 49. with good peel strength as well as adhesive. and retains strength at elevated tem.7 MPa 20. less Bulk Properties Tg Dry (°F / °C) 180 °F / 82 °C 230 °F / 110 °C 207 °F / 97 °C expensive and faster through-put. including laminating and injection. Injection Kit Clip Pack.800 psi / 60.000 psi / -55°C (Mpa)‘ 33. you need a two component system with a room temperature cure. waste and stress on components are (psi / MPa) reduced.000 psi / 34.6 MPa Henkel offers a high-performance structural adhesive portfolio in ready-to-use packaging 180°F (psi) / 2.90 GPa 375 ksi / 2.00 % 6. for repair of metal and composite structure.900 psi / 3.274 MPa 42 ksi / 2.3 MPa or make repairs to metallic substrates on the production line while improving your employ.300 psi / 2. Dual Cartridge. some toughness and maintains high peratures.6 MPa @ 77°F (psi) / 25°C (MPa) ›› Create durable repairs Compressive Modulus 265 ksi / 1. Quart Kit Barrier Kit.5 MPa 27. The down time is minimized. possesses elevated temperature resistance. Its room tem- temperature and yields durable bonds perature cure capability makes it ideal over a wide temperature range.00 % 9. you will surely Peel Strength High Low Low be looking for a solution that has high strength.1 MPa ees’ p ­ roductivity and safety. Honeycomb Bonding & Repair Characteristics 180°F / 82°C Service • • • 300°F / 149°C Service If you need a metal bond or repair solution with paste adhesives 350°F / 177°C Service LOCTITE is for you 450°F / 232°C Service Improved Hot / Wet Properties Toughened • • • Consistency Moderate Viscosity Thixotropic Low Viscosity Metal and Honeycomb bonding and repair solutions require maximum flexibility Form 2 Part 2 Part 2 Part When it comes to bonding or repair of metal parts and structures of an aircraft.00 MPa 8. This product cures at room temperature strength.58 GPa @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight LOCTITE metal bond and repair paste adhesives: (PartA / Part B) 100 : 19 100 : 50 100 : 45 Facts at a glance CureTemperature (°F / °C) > 77 – 200°F / > 25 – 93 °C 77 – 200 °F / 25 – 93 °C > 77 – 200 °F / > 25 – 93 °C CureTime 5 – 7 Days / 1 Hour 5 – 7 Days / 1 Hour 5 – 7 Days / 1 Hour StorageTemperature (°F / °C) 77 °F / 25 °C 40 °F / 4 °C 40 °F / 4 °C Pot Life 25 Minutes / 200 Gram Mass 40 Minutes / 450 Gram Mass 30 Minutes / 450 Gram Mass LOCTITE structural metal bond paste solutions key features (minutes / lb) / (minutes / kg) ›› Industry standard for metal bond applications ›› Easy application Product LOCTITE LOCTITE LOCTITE New Product Name EA 9320NA EA 9321 EA 9323 ›› Out-of-Autoclave solutions ›› Chemical resistance AERO AERO AERO Hysol® Hysol® Hysol® Known As EA 9320NA™ EA 9321™ EA 9323™ Key factors to consider when choosing the right LOCTITE structural repair product ›› Metal bond or composite to repair ›› High compression loads resistance Availability Packaging Quart Kit.1 MPa @ 77°F (psi) / 25°C (MPa) ›› Qualified by major OEM’s ›› Excellent resistance to aggressive chemicals Tensile Modulus to increase part life 330 ksi / 2. Finally.00 % @ 77°F / 25°C (% at break) ›› Superior mechanical strength ›› Room temperature and elevated cure Compressive Strength ­temperatures options 8.5 MPa 7.9 MPa 20. In addition.000 psi / 4.200 psi / ­configurations for aerospace OEM and MRO customers.500 psi / 24.6 MPa 27. which exhibits toughness which is low in viscosity. the ­efficiency is more than convincing thanks to a less time consuming. Honeycomb Bonding & Repair Characteristics 180°F / 82°C Service • • • • • • • 300°F / 149°C Service 350°F / 177°C Service 450°F / 232°C Service Improved Hot / Wet Pro- • • • • perties Toughened • • • • • • • Consistency Moderate Viscosity Thixotropic Thixotropic Thixotropic Thixotropic Thixotropic Moderate Viscosity Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength High High High High High High High Mechanical Bell Peel 77°F (lb / in) 92 lbs / in 93 lbs / in 75 lbs / in 60 lbs / in 50 lbs / in 40 lbs / in 44 lbs / in Properties 25°C (N / 25 mm) 409 N / 25 mm 414 N / 25 mm 335 N / 25 mm 265 N / 25 mm 178 N / 25 mm 220 N / 25 mm 196 N / 25 mm -67°F (psi) / 5.538 MPa 355 ksi / 2.500 psi / 17.000 psi / 5.900 psi / 4.200 psi / 4.7 MPa 29.000 psi / – 82°C (Mpa) 6.3 MPa 27.6 MPa 13.6 MPa 27.9 MPa 7.600 psi / 38.00 % 7.3 EA 9359.6 MPa 32.1 MPa 9.950 MPa – – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 33 100 : 33 100 : 44 100 : 43 100 : 55 100 : 45 100 : 35 (PartA / Part B) CureTemperature (°F / °C) 77 – 200 °F / 25 – 93 °C > 77 – 200 °F / > 25 – 93 °C 77 – 180 °F / 25 – 82 °C 77 – 180 °F / 25 – 82 °C ≥ 160 – 175 °F / 70 – 80 °C 180 – 220 °F / 82 – 104 °C > 77 °F / 25 °C CureTime 5 – 7 Days / 1 Hour 5 – 7 Days / 1 Hour 5 – 7 Days / 150 °F / 66 °C" StorageTemperature (°F / °C) 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C 5 – 7 Days / 1 Hour 240 Minutes 2 hours / 1 hour 5 Days / 1 Hour 60 Minutes / 100 Gram Mass / Pot Life 50 Minutes / 60 Minutes / 100 Gram Mass 60 Minutes / 100 Gram Mass 77 °F / 25 °C 40 °F / 4 °C 40 °F / 4 °C 82 °F / 28 °C (minutes / lb) / (minutes / kg) 200 Gram Mass / 40 Minutes / 450 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9330 EA 9330. Quart Kit – Gallon Kit LOCTITE LOCTITE LOCTITE LOCTITE LLOCTITE LOCTITE LOCTITE Description EA 9330 EA 9330.2 ksi / 3360 MPa – – – @ 77°F (ksi) / 25°C (MPa) Elongation 2.136 MPa 487.6 MPa TENSILE LAP SHEAR 77°F (psi) / 5. Dual Cartridge.0 MPa 27.3™ EA 9359.700 psi / 4. Barrier Kit.3 EA 9360 EA 9380 EA 9380. Honeycomb Bonding & Repair | 31 Structural Adhesives Paste Adhesives Metal.000 psi / 5.000 psi / – -55°C (Mpa)‘ 34.05 EA 9345 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9330™ EA 9330. Gallon Kit Dual Cartridge.5 MPa Elevated Temperature – – 1.000 psi / 1.8 MPa 31.743 MPa – – 368 ksi / 2.000 psi / 4.5 MPa 36.300 psi / 78 MPa – – @ 77°F (psi) / 25°C (MPa) Compressive Modulus 253 ksi / 1.646 MPa 390 ksi / 2.000 psi / 6.1 MPa 27.1 MPa 180°F (psi) / 1.6 MPa – – – – @ 77°F (psi) / 25°C (MPa) Tensile Modulus 384 ksi / 2.500 psi / 5.5 Mpa 33. Clip Pack Quart Kit.687 MPa 310 ksi / 2.1 MPa – 7.000 psi / 4.05 EA 9345™ Availability Packaging Barrier Kit.5 MPa 2.9 Mpa 35.000 psi / 3. toughness and high temp • Toughened • Room Temperature Cure • Easy Mix • High Shear Strength • >225°F (107°C) service resistance resistance • High Peel Strength • High Peel Strength • Bondline Thickness Control • Easy mixing two component system • Prebond humidity resistant • Prebond humidity resistant • Excellent Environmental Resistance • High Peel Strength • Room temperature cure • Available in 2:1 Dual Cartridge with • Low Slump Static Mixer .0 MPa 34. Metal.878 psi / 68 MPa 11.700 psi / 53.100 psi / 42.100 psi / 4.70 % 5.0 MPa 33.40 % 9.650 psi / 4.100 psi / 2.700 psi / 53.3 EA 9359.5 MPa 39.3 EA 9360 EA 9380 EA 9380.350 psi / 5.00 % – – – @ 77°F / 25°C (% at break) Compressive Strength 7. Gram Kit.000 psi / 4.750 psi / 12 MPa – (psi / MPa) Bulk Properties Tg Dry (°F / °C) 135 °F / 57 °C 129 °F / 54 °C 134°F / 51°C 151 °F / 66 °C 200 °F / 93 °C 223 °F / 106 °C 208 °F / 98 °C Tg Wet (°F / °C) – – 150 °F / 66 °C – 225 °F / 108 °C 192 °F / 89 °C 145 °F / 63 °C Tensile Strength 5.8 MPa 20.000 psi / 4.2 MPa 1.3™ EA 9360™ EA 9380™NEW! EA 9380.9 MPa 950 psi / 6.0 MPa 5300 psi / 36. Gallon Kit Quart Kit.05 EA 9345 AERO AERO AERO AERO AERO AERO AERO • Two Component System • Two Component System • Easy Mix • Available in dual cartridge packaging • Low temp curing two-part adhesive • Low temp curing two-part adhesive • Long Pot Life • Tolerant of Bondline Thickness • Low Slump • Good Environmental Resistance • High peel strength • Meter mixable • Meter mixable • Non-Asbestos Variations • Room Temperature Cure • Non Sag • Excellent static stress durability • High strength. Honeycomb Bonding & Repair Metal. Gallon Kit Quart Kit.800 psi / 25°C (Mpa) 34.6 MPa 6. Dual Cartridge. toughness and high temp • High strength. Pint Kit. Its room temperature cure temperature and possesses superior • High Shear Modulus • Room Temperature Storage Its thixotropic nature makes it ideal for pot.200 psi / 8. compressive strength make it ideal • Low Toxicity systems.000 psi / 82. • Outstanding Mechanical Properties ting. Gram Kit Barrier Kit. Dual Dual Cartridge. . Clip Quart Kit.500 psi / 2. Gram Kit. Gram Quart Kit.6 MPa @ 77°F (psi) / 25°C (MPa) Tensile Modulus 370 ksi / 2.5 MPa 24. adhesive.3 MPa 20. Gram Kit. Honeycomb Bonding & Repair Characteristics 180°F / 82°C Service • 300°F / 149°C Service • • • • • • 350°F / 177°C Service 450°F / 232°C Service • Improved Hot / Wet Pro- • • • perties Toughened • • • Consistency Low Viscosity Thixotropic Low Viscosity Thixotropic Thixotropic Moderate Viscosity Thixotropic Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength Nil Nil Nil Low Nil Low Low Mechanical Bell Peel 77°F (lb / in) 20 lbs / in 20 lbs / in 10 lbs / in 15 lbs / in – – – Properties 25°C (N / 25 mm) 89 N / 25 mm 90 N / 25 mm 45 N / 25 mm 67 N / 25 mm -67°F (psi) / 1.7 MPa 21.089 MPa 367 psi / 2.7 MPa 180°F (psi) / 1.9 MPa 34. Injection Kit.000 psi / 94. which cures at room • Good Wetting • Potting Material adhesive. injection. and liquid shim applications.700 psi / 11.200 psi / 56.500 psi / 2.8 MPa 25. Gallon Kit.8 MPa 9.3 MPa 21. It uses a non-aromatic amine curing • Thixotropic capability and low viscosity make it strength to 300 °F / 149 °C and hig.1 MPa 15.200 psi / 8. agent that retains many of the excellent • Excellent Mechanical Properties ideal for repair applications.552 MPa 550 ksi / 3.60% @ 77°F / 25°C (% at break) Compressive Strength 12. Honeycomb Bonding & Repair | 33 Structural Adhesives Paste Adhesives Metal. as well long pot life. Quart Kit Kit.1 MPa 32. Pint Kit.9 MPa 1.000 psi / 4. 5-Gallon Kit. Clip Pack Pint Kit.000 psi / 3.000 psi / 6. Quart Kit. Gallon Kit LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EA 956 EA 934NA EA 9390 EA 9394 EA 9394.7 MPa 20.6 MPa 24. high • Non-Metallic Filler has excellent elevated temperature paste adhesive.530 MPa – – – – 429 ksi / 2.2™ EA 9394™ / C-2™ EA 9395™ Availability Clip Pack.792 MPa 418 ksi / 2.2 MPa 22.8 MPa TENSILE LAP SHEAR 77°F (psi) / 2.9 MPa 28. Its thixotropic nature and good • Long Pot Life properties offered by aromatic amine cured • Good Compressive Strength laminating.100 psi / 2. Metal.237 MPa – – 717 ksi / 4. filling.500 psi / 17. high temperature service with a for potting. filling.9 MPa 33.200 psi / 8.500 psi / 82°C (Mpa) 10.7 MPa 18.1 MPa Elevated Temperature 1. sive.7 MPa 14.6 MPa 10.780 psi / 3.700 psi / 3.40 % 1. which cures at room temperature.0 MPa 8.5 MPa 5.3 MPa 2. Barrier 55-Gallon Kit.300 psi / -55°C (Mpa)‘ 12. including her.000 psi / 68.7 MPa 27.2 EA 9394/C-2 EA 9395 AERO AERO AERO AERO AERO AERO AERO is a two-component.2 EA 9394/C-2 EA 9395 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 956™ EA 934NA™ EA 9390™ EA 9394™ EA 9394.20 % 2. as for shim applications.800 psi / 40.93 °C 77 – 200 °F / 25 – 93 °C 250 °F / 121 °C 77 – 200 °F / 25 – 93 °C 77 °F / 25 °C > 200 °F / 93 °C 77 – 150 °F / 25 – 66 °C 300 °F / 149 °C 220 Minutes CureTime 5 – 7 Days / 1 Hour 5 – 7 Days / 1 Hour 150 Minutes 3 – 5 Days / 1 Hour 24 Hours 1 Hour 5 Days / 1 Hour 130 Minutes StorageTemperature (°F / °C) 40 °F / 4 °C 40 °F / 4 °C 40 °F / 4 °C 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C Pot Life > 30 minutes / 450 Gram Mass 40 – 50 minutes / 450 Gram Mass 120 Minutes / 250 Gram Mass 90 Minutes / 450 Gram Mass 20 – 30 Minutes / 100 Gram Mass 7 Hours / 450 Gram Mass 95 – 100 Minutes / 450 Gram Mass (minutes / lb) / (minutes / kg) LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 956 EA 934NA EA 9390 EA 9394 EA 9394.000 psi / 220.640 psi / 11.200 psi / 3.300 psi / 3.50 % 1. Quart Kit Pack. service temperature structural paste adhe.956 MPa @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 58 100 : 33 100 : 56 100 : 17 100 : 27 100 : 20 100 : 17 (PartA / Part B) 200 °F / 93 °C CureTemperature (°F / °C) 77 – 200 °F / 25 .200 psi / 4.329 psi / 78.77 % – – 2.600 psi / 4. Gallon Kit. and coating. Pint Kit.300 psi / 36.5 MPa 29.5 MPa 17. • Cures at Ambient Temperature strength.4 MPa 15.140 psi / 4.3 MPa 1.3 MPa (psi / MPa) Bulk Properties Tg Dry (°F / °C) 156 °F / 69 °C 159 °F / 71 °C 345 °F / 174 °C 172 °F / 78 °C 158 °F / 70 °C – 163 °F / 73 °C Tg Wet (°F / °C) – 235 °F / 113 °C 302 °F / 150 °C 154 °F / 68 °C 196 °F / 91 °C – 246 °F / 119 °C Tensile Strength 5. 5-Gallon Kit Kit. Clip Pack.000 psi / 3. Clip Pack.940 MPa @ 77°F (ksi) / 25°C (MPa) Elongation 2. Gallon Kit.800 psi / 3. which is a two-component thixotropic • Good Hot/Wet Strength • Good Gap Filling Capabilities is a fast curing two-part structural paste is an elevated temperature curing. Clip Pack. Honeycomb Bonding & Repair Metal.5 MPa 6. 5-Gallon Packaging Quart Kit.0 MPa – – 8.880 MPa 615 ksi / 4.500 psi / 65. Quart Kit“ Kit Cartridge.7 MPa 1.9 MPa 11.2 MPa 1.910 psi / 5. Clip Pack.5 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 158 ksi / 1. Injection Kit.700 psi / 2.300 psi / 25°C (Mpa) 15. and fairing.070 psi / 55.675 psi / 46.800 psi / 40.000 psi / 3.3 MPa 1.3 MPa 19.0 MPa 5.300 psi / 2. and fairing.6 MPa 7. Quart Kit Quart Kit Injection Kit Barrier Kit.2™ 50-Gram Kit.000 psi / 68.9 Mpa Elevated Temperature 1.100 psi / 4.237 MPa – – @ 77°F (ksi) / 25°C (MPa) Elongation 3.8 MPa 17.500 psi / 6.1 MPa 29.4 MPa 37.6 MPa 2.66 °C 200 °F / 93 °C 77 – 200 °F / 25 – 93 °C 77 °F / 25 °C 77 – 200 °F / 25 – 93°C 150 °F / 66 °C 180 °F / 82 °C CureTime 3 – 5 Days / 1 Hour 1 Hour 3 – 5 Days / 1 Hour 5 – 7 Day / 1 Hour 3 – 5 Days / 1 Hour 24 Hours 5 Days StorageTemperature (°F / °C) 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C 82 °F / 28 °C 82 °F / 28 °C 82 °F / 28 °C 82 °F / 28°C Pot Life 30 Minutes / 120 Minutes / 100 Gram Mass 7 Hours / 450 Gram Mass 120 Minutes / 100 Gram Mass 75 Minutes / 100 Gram Mass 90 Minutes / 450 Gram Mass 20 Minutes / 400 Gram Mass (minutes / lb) / (minutes / kg) 450 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9396 EA 9396/C-2 EA 9309NA EA 9392 EA 9394S EA 9891RP EA 9309. which is a two-component thixotropic • High Peel Strength is a paste adhesive.716 MPa – – 172. Honeycomb Bonding & Repair Characteristics 180°F / 82°C Service • • 300°F / 149°C Service • • 350°F / 177°C Service • • • 450°F / 232°C Service Improved Hot / Wet Pro- • • perties Toughened • • • • Consistency Low Viscosity Low Viscosity Moderate Viscosity Thixotropic Thixotropic Thixotropic Moderate Viscosity Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength Moderate Low High High Low Nil High Mechanical Bell Peel 77°F (lb / in) 25 lbs / in 15 lbs / in 25 lbs / in 40 lbs / in 20 lbs / in 40 lbs / in – Properties 25°C (N / 25 mm) 111 N / 25 mm 67 N / 25 mm 111 N / 25 mm 178 N / 25 mm 90 N / 25 mm 178 N / 25 mm -67°F (psi) / 3.000 psi / 96.300 psi / 4.5 MPa 7700 psi / 53 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 8. Gallon Kit.3 MPa 6.6 MPa 28. water and most common fluids. Clip Packaging Kit.2 Mpa 180°F (psi) / 3.000 psi / 482. outstanding feature is high shear and peel laminating. Barrier Availability Pint Kit.7 MPa 31.9 MPa 3. 5-Gallon Kit.6 MPa 6.40 % – 10. Quart Kit Pudding Cup. is a two-part structural paste adhesive. injection. Injection Kit Injection Kit.2 MPa – 1.000 psi / 41.7 MPa 42. Its thixotropic nature and good temperature range.2 MPa – 4.9 MPa 600 psi / 4.331 MPa 475 ksi / 3.70 % – 4.3 MPa 9. filling. which cures at room • Bonds Many Surfaces lent shear strength at high temperatures.7 MPa 3.000 psi / 525 psi / 1000 psi / 82°C (Mpa) 22.2 MPa 20.300 psi / 2. Gallon Kit. Gram Kit.00 % 4.500 psi / 3. Quart Kit.2 AERO AERO AERO AERO AERO AERO AERO is a two-component. including her.250 psi / 8.80% @ 77°F / 25°C (% at break) Compressive Strength 70. abrasion resistant repair paste skins and honeycomb core to yield tough strength.2 MPa 46. adhesive.500 psi / 31 MPa 6. Its ideal for repair applications. iis a two-component room temperature is a two part epoxy sytem bonds metal has excellent elevated temperature paste adhesive.00 % 1.600 psi / 6.0 MPa 28. Honeycomb Bonding & Repair | 35 Structural Adhesives Paste Adhesives Metal.8 MPa 14.1 MPa 31. and yields durable bonds over a wide excellent high temperature compressive 9890 AERO abradable seal. strength on aluminum bonds at moderate for potting. compressive strength make it ideal filling and liquid shim applications.300 psi / 4600 psi / – -55°C (Mpa)‘ 22.000 psi / 6.2 MPa 9. . Pint Kit.200 psi / 4.500 psi / 3.000 psi / 48.300 psi / 2.1 MPa 22.500 psi / 4.2 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9396™ EA 9396™ / C-2™ EA 9309NA™ EA 9392™ EA 9394S™ EA 9891RP™ EA 9309.650 psi / 5400 psi / 25°C (Mpa) 24.270 psi / 22. Its room temperature cure temperature and possesses superior This product exhibits excellent toughness temperatures. Metal.700 psi / 3.200 psi / 1.1 MPa – – (psi / MPa) Bulk Properties Tg Dry (°F / °C) 208 °F / 98 °C 226°F / 108°C 127 °F / 53 °C 164 °F / 73 °C 172 °F / 78 °C 248 °F / 120 °C 174°F / 79°C Tg Wet (°F / °C) 145 °F / 63 °C 232°F / 111°C 147 °F / 64 °C 144 °F / 62 °C 154 °F / 68 °C – 138°F / 59°C Tensile Strength 8.2 Mpa @ 77°F (psi) / 25°C (MPa) Tensile Modulus 400 ksi / 2.000 psi / 55. Quart Kit Pack.500 psi / 17.273 MPa 615 ksi / 4. which possesses excellent strength at high curing.750 MPa – 338 ksi / 2.0 MPa – 5400 psi / 37.7 Mpa TENSILE LAP SHEAR 77°F (psi) / 3.1 MPa 10. Honeycomb Bonding & Repair Metal. which possesses excel. strength also make it ideal for potting. and coating. midity.0 MPa 17.675 psi / 46. as for shim applications.2 MPa 24.9 MPa 11.5 ksi / 1.188 MPa 218 Ksi / 1502 MPa @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 30 100 : 36 100 : 30 100 : 32 – 100 : 40 100 : 22 (PartA / Part B) 77 °F / 25 °C 77 °F / 25 °C CureTemperature (°F / °C) 77 – 150 °F / 25 . as well temperatures.150 MPa – 249 ksi / 1. Quart Kit LOCTITE LOCTITE LOCTITE LOCTITE Loctite LOCTITE LOCTITE Description EA 9396 EA 9396/C-2 EA 9309NA EA 9392 EA 9394S EA 9891RP EA 9309. Its thixotropic nature and adhesive suitable for repairing LOCTITE EF permanently flexible joints that resist hu- capability and low viscosity make it strength to 300 °F / 149 °C and hig.100 psi / 1.300 psi / 64. Clip Pack.000 psi / 55. Bulk Properties Tg Dry (°F / °C) 142 °F / 61 °C 135 °F / 57 °C 129 °F / 54 °C Why choose LOCTITE composite bonding adhesives? Tg Wet (°F / °C) 147 °F / 64 °C – – ›› Easy to mix Tensile Strength 4.646 MPa 390 ksi / 2.5 MPa 39.0 MPa ›› Good environmental resistance @ 77°F (psi) / 25°C (MPa) Tensile Modulus ›› Sag resistant @ 77°F (ksi) / 25°C (MPa) 334 ksi / 2.700 psi / 53.5 MPa 34. Gallon Kit Quart Kit.0 MPa 34.688 MPa 253 ksi / 1.7 MPa 7.00 % 2.3NA AERO EA 9330 AERO EA 9330.3 AERO ›› Viscosity ›› Cure temperature • High Shear Strength • Two Component System • Two Component System • High Peel Strength • Tolerant of Bondline Thickness • Low Slump ›› Shelf life / out-time ›› Glass transition temperature (Tg) • Bondline Thickness Control Variations • Room Temperature Cure • Good Environmental Resistance • Room Temperature Cure • Easy Mix • High Peel Strength • High Peel Strength • Excellent Environmental Resistance .743 MPa – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 22 100 : 33 100 : 33 LOCTITE composite bonding adhesives: (PartA / Part B) 77 °F / 25 °C CureTemperature (°F / °C) 77 – 200 °F / 25 – 93 °C > 77 – 200 °F / > 25 – 93 °C Facts at a glance 180 °F / 82 °C“ CureTime 3 – 5 Days / 1 Hour 5 – 7 Days / 1 Hour 5 – 7 Days / 1 Hour StorageTemperature (°F / °C) 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C Pot Life 35 minutes / 60 Minutes / 60 Minutes / LOCTITE composite bonding adhesives key features: (minutes / lb) / (minutes / kg) 450 Mram Mass 100 Gram Mass 100 Gram Mass ›› High service temperature ›› Toughness tailorable to requirements Product LOCTITE LOCTITE LOCTITE New Product Name EA 9309.687 MPa ›› High shear & peel strength Elongation 10.3 ›› Prepreg ›› Variations in form: One or two part AERO AERO AERO ›› Compatibility with aerospace systems ›› Variable viscosity to fit application requirements Known As Hysol® Hysol® Hysol® EA 9309.700 psi / -55°C (Mpa)‘ 38.100 psi / 42. let 82°C (Mpa) 5.3NA™ EA 9330™ EA 9330. Gram Kit.1 MPa – @ 77°F (psi) / 25°C (MPa) Compressive Modulus 245 ksi / 1.500 psi / 5. some questions might come up Peel Strength High High High In order to preserve the structural integrity of critical aircraft components.000 psi / 5.000 psi / 4.5 Mpa 33.303 MPa 384 ksi / 2. -67°F (psi) / 5. Clip Pack tion Kit. variable viscosity and extraordinary mechanical performance. Injec- Packaging Barrier Kit.900 psi / 25°C (Mpa) 34.9 MPa 7. manufacturers Mechanical Bell Peel 77°F (lb / in) 94 lbs / in 92 lbs / in 93 lbs / in need the right adhesives to bond or join composite sub-components with excellent chemical Properties 25°C (N / 25 mm) 418 N / 25mm 409 N / 25 mm 414 N / 25 mm ­resistance. Gram Kit.000 psi / 5.3 MPa TENSILE LAP SHEAR Henkel gives a strong answer: LOCTITE composite bonding adhesives 77°F (psi) / 5.40 % 9.100 psi / create efficient structures.500 psi / 51.6 MPa 6. Gallon Kit. Composite Bonding and Repair Composite Bonding and Repair | 37 Structural Adhesives Paste Adhesives Composite Bonding and Repair Characteristics 180°F / 82°C Service • • • 300°F / 149°C Service When structural integrity matters: 350°F / 177°C Service LOCTITE composite bonding 450°F / 232°C Service Improved Hot / Wet Pro- and repair adhesives • perties Toughened • • • Consistency Moderate Viscosity Moderate Viscosity Thixotropic Form 2 Part 2 Part 2 Part Concerning critical aircraft components. They offer lower adherent thickness. solvents and water ›› High mechanical performance Availability Clip Pack.670 psi / 32.3NA EA 9330 EA 9330.2 MPa 6.8 Mpa LOCTITE products for composite bonding fulfill all these requirements and allow engineers to 180°F (psi) / 750 psi / 1. No fasteners are needed.600 psi / 38. Quart Kit Key factors to consider when choosing the right LOCTITE composite bonding adhesive LOCTITE LOCTITE LOCTITE Description EA 9309.2 MPa 5.00 % @ 77°F / 25°C (% at break) ›› Bond line thickness control Compressive Strength 7.3™ ›› Good wetting of metallic and composite surfaces ›› Excellent chemical resistance vs.000 psi / 1.6 MPa you take advantage of stiffness properties of composites and provide a separation of dissimilar Elevated Temperature – – – (psi / MPa) materials. 500 psi / 17.200 psi / 3.5 MPa 36. Pint Kit. Dual Cartridge. Barrier Kit.200 psi / 4. toughness and high temp mechanical performance.180 °F / 25 – 82 °C 77 – 180 °F / 25 – 82 °C ≥ 160 – 175 °F / 70 – 80 °C 180 – 220 °F / 82 – 104 °C 250 °F / 121 °C 77 – 200 °F / 25 – 93 °C 180 °F / 83 °C“ 300 °F / 149 °C“ 220 Minutes CureTime 5 – 7 Days / 1 Hour 5 – 7 Days/ 1 Hour 240 Minutes 2 hours / 1 hour 5 – 7 Days / 1 Hour 150 Minutes 3 – 5 Days / 1 Hour 130 Minutes StorageTemperature (°F / °C) 77 °F / 25 °C 77 °F / 25 °C 40 °F / 4 °C 40 °F / 4 °C 77 °F / 25 °C 40 °F / 4 °C 77 °F / 25 °C 60 Minutes / 100 Gram Mass / Pot Life 50 Minutes / 50 Minutes / 180 Minutes / 300 Minutes / 60 Minutes / 120 Minutes / 90 Minutes/ (minutes / lb) / (minutes / kg) 200 Gram Mass / 200 Gram Mass 500 Gram Mass 500 Gram Mass 20 Gram Mass 250 Gram Mass 450 Gram Mass 40 Minutes / 450 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9359.000 psi / 3. Quart Kit LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EA 9359. • Low temp curing two-part adhesive • Low temp curing two-part adhesive is a two-component flame retardant • Good Hot/Wet Strength • Good Gap Filling Capabilities • Good Environmental Resistance aging • Meter mixable • Meter mixable toughened paste adhesive. • Long Pot Life • High Peel Strength • Easy mixing two component system • Low Toxicity • Available in 2:1 Dual Cartridge with • Room temperature cure Static Mixer • Low Slump .5 MPa 6.000 psi / 5.70 % 5. Clip Pack.6 MPa – – – – 8.9 MPa 950 psi / 6.3 EA 9360 EA 9380 EA 9380.950 MPa – – – – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 44 100 : 43 100 : 55 100 : 45 100 : 42.136 MPa 487.700 psi / 53. Gram Kit.50 % 1.500 psi / 5. It contains no • High Shear Modulus • Room Temperature Storage • High Shear Strength • Excellent static stress durability temp resistance resistance halogenated resins common in many other • Outstanding Mechanical Properties • Bondline Thickness Control • >225°F (107°C) service • Prebond humidity resistant • Prebond humidity resistant flame retardant products.650 psi / 4.9 MPa 180°F (psi) / 2. Barrier Kit Gallon Kit“ Cartridge.000 psi / 6.000 psi / 2.538 MPa 355 ksi / 2.237 MPa @ 77°F (ksi) / 25°C (MPa) Elongation 7. Dual Cartridge. Gram Kit.1 MPa 9. Clip Pack.5 Mpa 2.000 psi / 4.100 psi / 4.0 MPa 27. Dual Packaging Quart Kit.05 EA 9364FR™ EA 9390™ EA 9394™ Availability Quart Kit.9 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus – 368 ksi / 2.05 EA 9364FR EA 9390 EA 9394 AERO AERO AERO AERO AERO AERO AERO • Easy Mix • Available in dual cartridge pack.00 % – – – 2.5 MPa 20. Composite Bonding and Repair Composite Bonding and Repair | 39 Structural Adhesives Paste Adhesives Composite Bonding and Repair Characteristics 180°F / 82°C Service • • • • • 300°F/149°C Service • • 350°F / 177°C Service 450°F / 232°C Service Improved Hot / Wet Pro- • • • • • • perties Toughened • • • • • Consistency Thixotropic Thixotropic Thixotropic Thixotropic Moderate Viscosity Low Viscosity Thixotropic Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength High High High High Low Nil Low Mechanical Bell Peel 77°F (lb / in) 75 lbs / in 60 lbs / in 50 lbs / in 40 lbs / in 20 lbs / in 20 lbs / in – Properties 25°C (N / 25 mm) 335 N / 25 mm 265 N / 25 mm 178 N / 25 mm 220 N / 25 mm 89 N / 25 mm 89 N / 25 mm -67°F (psi) / 4.05 EA 9364FR EA 9390 EA 9394 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9359.3 EA 9360 EA 9380 EA 9380.000 psi / 68.2 MPa 1. Gallon Kit Dual Cartridge.3 MPa (psi / MPa) Bulk Properties Tg Dry (°F / °C) 134°F / 51°C 151 °F / 66 °C 200 °F / 93 °C 223 °F / 106 °C – 345 °F / 174 °C 172 °F / 78 °C Tg Wet (°F / °C) 150 °F / 66 °C – 225 °F / 108 °C 192 °F / 89 °C – 302 °F / 150 °C 154 °F / 68 °C Tensile Strength 5300 psi / 36.000 psi / – 82°C (Mpa) 13.6 MPa 10.0 MPa 34.6 MPa 32.7 MPa TENSILE LAP SHEAR 77°F (psi) / 4.300 psi / – -55°C (Mpa)‘ 27.0 MPa @ 77°F (psi) / 25°C (MPa) Tensile Modulus 310 ksi / 2.370 psi / 2.878 psi / 68 MPa 11. 55-Gallon Kit.700 psi / 11. 5-Gallon Kit.4 100 : 56 100 : 17 (PartA / Part B) 200 °F / 93 °C > 77 °F / 25 °C CureTemperature (°F / °C) 77–.200 psi / 8.000 psi / 3.000 psi / 4.77% @ 77°F / 25°C (% at break) Compressive Strength 7.2 MPa 22.000 psi / 3.9 MPa 28.7 MPa 29.2 ksi / 3360 MPa – – – 418 ksi / 2.200 psi / 56.1 MPa 27.675 psi / 46.300 psi / 78 MPa – – 5.6 MPa 15. Quart Kit – – Quart Kit.300 psi / 36.1 MPa 17.880 MPa 615 ksi / 4.000 psi / 4.3™ EA 9360™ EA 9380™NEW! EA 9380. toughness and high • High strength. with excellent • Good Wetting • Potting Material • Non Sag • High peel strength • High strength.7 MPa Elevated Temperature 1.6 MPa 27.750 psi / 12 MPa – 1.9 Mpa 35.7 MPa 20.600 psi / 4.350 psi / 5.7 MPa 1.200 psi / 25°C (Mpa) 31.8 MPa 20.0 MPa 30. Gram Kit.8 MPa 14.7 MPa 24.000 psi / 4.2 MPa TENSILE LAP SHEAR 77°F (psi) / 4.6 MPa 2.6 MPa 8. which cures at room • Non-Asbestos adhesive.000 psi / 96.200 psi / 8.500 psi / 17. and tensile lap shear strength at 200 °F agent that retains many of the excellent • Excellent Mechanical Properties • High Strength at Low and High Tem.2 MPa – @ 77°F (psi) / 25°C (MPa) Tensile Modulus – – – – 717 ksi / 4. Gallon Kit Pint Kit.7 MPa 14.9 MPa 33.910 psi / 4.66 °C 200 °F / 93 °C 150 °F / 66 °C“ 150 °F / 66 °C“ CureTime 24 Hours 5 Days / 1 Hour 5 –7 Days / 2 Hours 1 Hour 5 Days / 1 Hour 3 – 5 Days / 1 Hour 1 Hour StorageTemperature (°F / °C) 77 °F / 25 °C 82 °F / 28 °C 82 °F / 28 °C 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C Pot Life 20 – 30 Minutes / 90 Minutes/ 30 Minutes / 7 Hours / 95 – 100 Minutes / 120 Minutes / 7 Hours / (minutes / lb) / (minutes / kg) 100 Gram Mass 400 Gram Mass 100 Gram Mass 450 Gram Mass 450 Gram Mass 100 Gram Mass 450 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9394. Quart Kit.1 MPa 22.2 MPa (psi / MPa) Bulk Properties Tg Dry (°F / °C) 158 °F / 70 °C 208 °F / 98 °C – – 163 °F / 73 °C 208 °F / 98 °C 226°F / 108°C Tg Wet (°F / °C) 196 °F / 91 °C 145 °F / 63 °C – – 246 °F / 119 °C 145 °F / 63 °C 232°F / 111°C Tensile Strength – – – – 8.2 EA 9345 EA 9363 EA 9394/C-2 EA 9395 EA 9396 EA 9396/C-2 AERO AERO AERO AERO AERO AERO AERO is a fast curing two-part structural • Long Pot Life is a two-component toughened paste is an elevated temperature curing.300 psi / 3.5 MPa 24.8 MPa 17. Its thixotropic nature • Toughened strength at room temperature with sive.000 psi / 482. Barrier Kit.300 psi / 2.3 MPa – – 2.0 MPa 28.1 MPa 15. properties offered by aromatic amine cured • Good Compressive Strength peratures systems. Gallon Kit Quart Kit. high temperature service with a long pot life.250 psi / 8.940 MPa 400 ksi / 2. Composite Bonding and Repair Composite Bonding and Repair | 41 Structural Adhesives Paste Adhesives Composite Bonding and Repair Characteristics 180°F / 82°C Service • • 300°F/149°C Service • • • • 350°F / 177°C Service 450°F / 232°C Service • Improved Hot / Wet Pro- • • • perties Toughened • • • • • Consistency Thixotropic Moderate Viscosity Moderate Viscosity Moderate Viscosity Thixotropic Low Viscosity Low Viscosity Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength Nil High High Low Low Moderate Low Mechanical Bell Peel 77°F (lb / in) 20 lbs / in 44 lbs / in 65 lbs / in 10 lbs / in 15 lbs / in 25 lbs / in 15 lbs / in Properties 25°C (N / 25 mm) 90 N / 25 mm 196 N / 25 mm 289 N / 25 mm 45 N / 25 mm 67 N / 25 mm 111 N / 25 mm 67 N / 25 mm -67°F (psi) / 2.500 psi / 4. Injection Kit.600 psi / 25°C (Mpa) 33.1 MPa – – 32. • Cures at Ambient Temperature • Room Temperature Cure • Long Work Life temperature.140 psi / 3. Quart Kit Clip Pack.100 psi / – 82°C (Mpa) 21.329 psi / 78. Clip Pack Pack.5 MPa 29. 5-Gallon Packaging Gallon Kit 5-Gallon Kit.750 MPa – @ 77°F (ksi) / 25°C (MPa) Elongation – – – – 2.8 MPa 22. Clip Pack.500 psi / – -55°C (Mpa)‘ 18.300 psi / 3.6 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus – – – – 429 ksi / 2. Pint Kit.070 psi / 55.2 EA 9345 EA 9363 EA 9394/C-2 EA 9395 EA 9396 EA 9396/C-2 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9394.700 psi / 6.3 MPa 1.1 MPa 31.200 psi / 4.2 MPa 1. / 93 °C. Injection Kit.500 psi / 3. which combines high peel service temperature structural paste adhe.5 MPa 70. Gallon Kit.150 MPa – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 27 100 : 35 100 : 43 100 : 20 100 : 17 100 : 30 100 : 36 (PartA / Part B) > 77 °F / 25 °C > 77 °F / 25 °C CureTemperature (°F / °C) 77 °F / 25 °C > 200 °F / 93 °C 77 – 150 °F / 25 .956 MPa 8.500 psi / 2. • Ideal for use as Neat Lay-up Resin liquid shim applications. Gallon Kit.2™ EA 9345™ EA 9363™ EA 9394™ / C-2™ EA 9395™ EA 9396™ EA 9396™ / C-2™ 50-Gram Kit.1 MPa 45 MPa 34. 5-Gallon Kit Kit. 5-Gallon Kit.7 MPa 25 MPa 27. Clip Availability Dual Cartridge.500 psi / 17.60 % 3.625 psi / 4.40 % – @ 77°F / 25°C (% at break) Compressive Strength 11.7 MPa 180°F (psi) / 3.000 psi / 94. high • Non-Metallic Filler • Low Viscosity • Low Viscosity paste adhesive. Quart Kit. Injection Kit.525 psi / 3. Quart Kit“ LOCTITE LOCTITE LOCTITE LOCTITE LLOCTITE LOCTITE LOCTITE Description EA 9394. filling. It uses a non-aromatic amine curing • Thixotropic • Room Temperature Storage • Non-MDA Curing Agent makes it ideal for potting.66 °C 77 – 150 °F / 25 .000 psi / 55. .525 psi / 5.000 psi / 3.3 MPa Elevated Temperature 1.000 psi / 55.800 psi / 6.000 psi / 220.640 psi / 11.6 MPa 45 MPa 24. Injection Kit Kit.2 MPa 24.9 Mpa Elevated Temperature – 1.2 MPa 20.93°C 77 – 160 °F / 25 – 71 °C 77 – 200 °F / 25 – 93°C 150 °F / 66 °C“ 180 °F / 82 °C“ 25 – 93 °C“ CureTime 3 – 5 Days / 1 Hour 5 – 7 Day / 1 Hour 3 – 5 Days/ 1 Hour 5 – 7 Days / 1 Hour 24 Hours / 1 Hour 5 Days StorageTemperature (°F / °C) 77 °F / 25 °C 82 °F / 28 °C 82 °F / 28 °C 77 °F / 25 °C 77 °F / 25 °C 82 °F / 28°C Pot Life 120 Minutes / 75 Minutes / 90 Minutes / 25 Minutes / 30 minutes / 30 Minutes / (minutes / lb) / (minutes / kg) 100 Gram Mass 100 Gram Mass 450 Gram Mass 200 Gram Mass 100 Gram Mass 450 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9309NA EA 9392 EA 9394S EA 9320NA EA 960F EA 9309. outstanding feature is high shear and peel range.7 Mpa TENSILE LAP SHEAR 77°F (psi) / 6. Quart Kit LOCTITE LOCTITE Loctite LOCTITE LOCTITE LOCTITE Description EA 9309NA EA 9392 EA 9394S EA 9320NA 960F EA 9309. Composite Bonding and Repair Composite Bonding and Repair | 43 Structural Adhesives Paste Adhesives Composite Bonding and Repair Characteristics 180°F / 82°C Service • • 300°F/149°C Service • 350°F / 177°C Service • • • 450°F / 232°C Service Improved Hot / Wet Pro- perties Toughened • • • • Consistency Moderate Viscosity Thixotropic Thixotropic Moderate Viscosity Thixotropic Moderate Viscosity Form 2 Part 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength High High Low High Nil High Mechanical Bell Peel 77°F (lb / in) 25 lbs / in 40 lbs / in 20 lbs / in 35 lbs / in 40 lbs / in – Properties 25°C (N / 25 mm) 111 N / 25 mm 178 N / 25 mm 90 N / 25 mm 150 N / 25 mm 178 N / 25 mm -67°F (psi) / 6. Quart Kit Pack.300 psi / 2.1 MPa 29.00 % 1. temperatures.2 Mpa @ 77°F (psi) / 25°C (MPa) Tensile Modulus 338 ksi / 2.9 MPa 4.2 AERO AERO AERO AERO AERO AERO • High Peel Strength is a paste adhesive.200 psi / 5. It is a two.237 MPa 330 ksi / 2.9 MPa 34.2 Mpa 180°F (psi) / 1.7 MPa 33.273 MPa 615 ksi / 4. . Injection Kit Pudding Cup.1 MPa 10.000 psi / 48.716 MPa – – 265 ksi / 1.70 % 9. Clip 50-Gram Kit.2 MPa 37.7 MPa 15.000 psi / 41.100 psi / 4.3 MPa 6.2 AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9309NA™ EA 9392™ EA 9394S™ EA 9320NA™ EA 960F™ EA 9309.000 psi / 2. which cures rapidly permanently flexible joints that resist hu- excellent toughness and yields dura. 5-Gallon Kit. component system. skins and honeycomb core to yield tough temperatures.9 MPa 8. Clip Pack.000 psi / 2. Its temperature resistance.8 MPa 31. This product exhibits strength at high temperatures. Gallon Packaging Quart Kit Injection Kit Quart Kit.826 MPa – 218 Ksi / 1502 MPa @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 30 100 : 32 – 100 : 19 100 : 50 100 : 22 (PartA / Part B) 77 °F / 25 °C 77 °F / 25 °C 77 – 200 °F / CureTemperature (°F / °C) > 77 – 200°F / > 25 . water and most common fluids.200 psi / 5400 psi / 25°C (Mpa) 42. Quart Kit.80% @ 77°F / 25°C (% at break) Compressive Strength 7.900 psi / 2.8 MPa 6.000 psi / 55. thixotropic nature and excellent high at room temperature.675 psi / 46.000 psi / 6.0 MPa 17.274 MPa – – @ 77°F (ksi) / 25°C (MPa) Elongation 10.0 MPa 5. which possesses excellent good peel strength as well as elevated for exterior aircraft surfaces. Gallon Kit.500 psi / 3.1 MPa – 7700 psi / 53 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 249 ksi / 1.2™ Availability Pint Kit.8 MPa 13.6 MPa 28.2 MPa 9.9 MPa 600 psi / 4.331 MPa 475 ksi / 3.500 psi / 3.000 psi / 68. filling strength on aluminum bonds at moderate and liquid shim applications.5 MPa 2200 psi / 15. Its ble bonds over a wide temperature temperature compressive strength identify when fully mixed.000 psi / 4600 psi / -55°C (Mpa)‘ 46.2 MPA 5400 psi / 37.1 MPa – – – (psi / MPa) Bulk Properties Tg Dry (°F / °C) 127 °F / 53 °C 164 °F / 73 °C 172 °F / 78 °C 180 °F / 82 °C 150 °F / 66 °C 174°F / 79°C Tg Wet (°F / °C) 147 °F / 64 °C 144 °F / 62 °C 154 °F / 68 °C – 175 °F / 79 °C 138°F / 59°C Tensile Strength 4.700 psi / 3.00 % – 4. Gallon Kit.00 % 4. also make it ideal for potting.300 psi / 4.300 psi / 4.300 psi / 700 psi / 1000 psi / 82°C (Mpa) 9.300 psi / 64.500 psi / 31 MPa 6.1 MPa 22.5 MPa 15. It is color coded to midity. which possesses is a two-part structural paste is a two-component paste adhesive with iis a fairing and smoothing compound is a two part epoxy sytem bonds metal • Bonds Many Surfaces excellent shear strength at high adhesive.000 psi / 34. antimony and phenol-free. They are t­ oughened paste adhesive with superior dispense rate and high compressive strength potting compound. which may be products. By using the right fire retardant on honeycomb panels for edge close out. LOCTITE flame retardants are halogens. Especially developed for the highest safety standards: LOCTITE fire retardant Henkel has developed special flame retardant products for aircraft interior applications. with excellent mechanical supplied as a fil for core splicing and closeout of performance. antimony and ›› Slump resistant ›› Excellent strength after cure ­phenol-free Characteristics 180°F / 82°C Service • • 350°F / 177°C Service Consistency Moderate Viscosity Form 2 Part Peel Strength Low Mechanical 20 lbs / in Bell Peel @ 77°F (lb / in) / 25°C (N / 25 mm) – 89 N / 25 mm Properties TENSILE LAP SHEAR 77°F (psi) / 25°C (Mpa) 4. fire breakout is one of the most dangerous incidents. It contains no halogenated honeycomb panels. insert bonding or potting. which is ned paste adhesive. Composite Bonding and Repair Fire Retardants | 45 Structural Adhesives Paste Adhesives Notes LOCTITE fire retardant Be sure to protect your aircraft from fire For aircrafts. is an expanding foam adhesive. aircraft manufacturers can do their best to protect their aircraft. Gallon Kit Sheet LOCTITE LOCTITE Description EA 9364FR AERO EF 562SFR AERO is a two-component flame retardant toughe. It offers the advantaes of a resins common in many other flame retardant fire retardant structural adhesive. Why choose LOCTITE fire retardant? ›› Easy to apply ›› Provide excellent mechanical ›› Offer long mixed working life ›› Room temperature storage properties ›› Supplied in cartridges LOCTITE fire retardant: Facts at a glance LOCTITE fire retardants key features: ›› Two component product ›› Halogens.1 MPa – Handling Mix RatioWeight (PartA / Part B) 100 : 42.4 > 77 °F / 25 °C 250 °F / 121 °C CureTemperature (°F / °C) 180 °F / 83 °C or 350 °F / 177 °C 5 – 7 Days / CureTime 90 Minutes / 60 Minutes 1 Hour StorageTemperature (°F / °C) 77 °F / 25 °C 0 °F / -18 °C Pot Life (minutes / lb) / (minutes / kg) 60 Minutes / 20 Gram Mass – LOCTITE Product LOCTITE New Product Name EA 9364FR EF 562SFR AERO AERO Known As Hysol® EA 9364FR™ Hysol® MA 562SFR™ Availability Packaging Dual Cartridge.370 psi / 30. cured at 250 °F / 121 °C or 350 °F / 177 °C . 0 MPa – – ›› Good gap filling capabilities @ 77°F (psi) / 25°C (MPa) ›› Fast cure time Tensile Modulus 615 ksi / 4. Dual Cartridge. Bulk Properties Tg Dry (°F / °C) 172 °F / 78 °C 153 °F / 67 °C 151 °F / 66 °C Tg Wet (°F / °C) 154 °F / 68 °C – – Why choose LOCTITE liquid shims? Tensile Strength 6.2 ksi / 3360 MPa @ 77°F (ksi) / 25°C (MPa) ›› Tough – resistance to microcracking Elongation 1.538 MPa @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight (PartA / 100 : 17 100 : 55 100 : 43 Part B) LOCTITE liquid shims: CureTemperature (°F / °C) CureTime 77 – 200 °F / 25 – 93 °C 3 – 5 Days / 1 Hour ≥ 160 – 175 °F / 70 – 80 °C 240 Minutes 77 – 180 °F / 25 – 82 °C 5 – 7 Days/ 1 Hour Facts at a glance StorageTemperature (°F / °C) Pot Life (minutes / lb) / 77 °F / 25 °C 90 Minutes 40 °F / 4 °C 180 Minutes 77 °F / 25 °C 50 Minutes (minutes / kg) 450 Gram Mass 500 Gram Mass 200 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE liquid shims key features: Product New Product Name EA 9394 EA 9377 EA 9360 ›› Two-part custom filled epoxy-based materials ›› Ambient temperature storage AERO AERO AERO Hysol® Hysol® Hysol® ›› Extremely high compressive strength ›› Ambient & elevated temperature cure Known As EA 9394™ EA 9377™ EA 9360™ 55-Gallon Kit. 82°C (Mpa) 20.950 MPa 368 ksi / 2.300 psi / 78 MPa 9. Clip Pack.0 MPa 20. Clip Pack.9 MPa 36.000 psi / 68.237 MPa – 487. For gaps less than 3 millimeters or for wide area fit up. Mechanical Bell Peel 77°F (lb / in) 20 lbs / in 50 lbs / in 60 lbs / in liquid shims are employed. Properties 25°C (N / 25 mm) 89 N / 25 mm 178 N / 25 mm 265 N / 25 mm This forces any excess shim material to be squeezed out leaving just the necessary amount of -67°F (psi) / 3.9 MPa 34.350 psi / 5.500 psi / 17. Availability Barrier Kit. Gallon Kit Quart Kit ›› Good compression properties ›› Temperature performance LOCTITE LOCTITE LOCTITE ›› Fluid resistance: fuel. 5-Gallon Kit. Liquid Shim Liquid Shim | 47 Structural Adhesives Paste Adhesives Liquid Shim Characteristics 180°F / 82°C Service • • 300°F / 149°C Service • We mind the gaps for you with 350°F / 177°C Service LOCTITE liquid shims Improved Hot / Wet Pro- perties • • Toughened • • Consistency Thixotropic Thixotropic Thixotropic Form 2 Part 2 Part 2 Part The way to eliminate small gaps Peel Strength Low High High Whenever gaps and differences between two composite parts occur.878 psi / 68 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus – 355 ksi / 2. squeezed together and bolted.200 psi / 3.6 MPa TENSILE LAP SHEAR 77°F (psi) / 4. They are spread on one side of the rib.300 psi / 4.2 MPa 950 psi / 6. Quart Kit.1 MPa 27.7 MPa 32. Gram Kit. Injec- Key factors to consider when choosing the right LOCTITE liquid shim Packaging Dual Cartridge.7 MPa 29.5 Mpa (psi / MPa) and shim. They operate as both. Pint Kit.650 psi / 4.200 psi / 8.3 MPa 2.9 MPa 11.000 psi / shim to bridge any gaps occurring in the manufacturing process. water ingression ›› Low slump: low flow on vertical surfaces Description EA 9394 EA 9377 EA 9360 AERO AERO AERO ›› Adhesion properties: must bond well to substrate • Good Gap Filling Capabilities is a two-component moldable plastic • Available in dual cartridge pack- • Potting Material shim with excellent microcrack resis. -55°C (Mpa)‘ 22. shims both in solid and liquid form are used to eliminate them.000 psi / 4. offer good compressive strength across a wide temperature range and allow a long out time to facilitate larger parts.000 psi / LOCTITE liquid shims are epoxy-based materials that provide not only high compressive strength.7 MPa but also a balance between open assembly time and strength.5 MPa Guaranteeing a perfect result: LOCTITE liquid shims 180°F (psi) / 3. Gram Kit Quart Kit.675 psi / 46. an adhesive Elevated Temperature 1.77 % – 5.200 psi / 5.000 psi / 25°C (Mpa) 28.00 % @ 77°F / 25°C (% at break) ›› Qualified at most commercial aircraft OEMs Compressive Strength ›› Optimized to match CTE difference on composite substrates 10. tion Kit. aging • Room Temperature Storage tance under thermal cycling and high • High peel strength • Outstanding Mechanical Properties compressive strength • Excellent static stress durability • Long Pot Life • >225°F (107°C) service • Low Toxicity • Easy mixing two component system • Room temperature cure • Low Slump . Barrier Kit.300 psi / 36.7 MPa (psi / MPa) Bulk Properties Tg Dry (°F / °C) 200 °F / 93 °C 223 °F / 106 °C 158 °F / 70 °C 172 °F / 78 °C 345 °F / 174 °C Tg Wet (°F / °C) 225 °F / 108 °C 192 °F / 89 °C 196 °F / 91 °C 154 °F / 68 °C 302 °F / 150 °C Tensile Strength – – – 6.640 psi / 11.675 psi / 46.910 psi / 4. which cures at room which possesses excellent strength at high • Good Wetting • High strength.650 psi / 4.7 MPa 20.950 MPa – – – – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight (PartA / 100 : 55 100 : 45 100 : 27 – 100 : 56 Part B) 200 °F / 93 °C CureTemperature (°F / °C) ≥ 160 – 175 °F / 70 – 80 °C 180 – 220 °F / 82 – 104 °C 77 °F / 25 °C 77 – 200 °F / 25 – 93 °C 250 °F / 121 °C 300 °F / 149 °C 220 Minutes CureTime 240 Minutes 2 hours / 1 hour 24 Hours 3 – 5 Days / 1 Hour 150 Minutes 130 Minutes StorageTemperature (°F / °C) 40 °F / 4 °C 40 °F / 4 °C 77 °F / 25 °C 82 °F / 28 °C 40 °F / 4 °C Pot Life (minutes / lb) / 180 Minutes 300 Minutes 20 – 30 Minutes 90 Minutes 120 Minutes (minutes / kg) 500 Gram Mass 500 Gram Mass 100 Gram Mass 450 Gram Mass 250 Gram Mass LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 9380 EA 9380.7 MPa Elevated Temperature 2.0 MPa 8. 5-Gallon Kit LOCTITE LOCTITE LLOCTITE Loctite LOCTITE Description EA 9380 EA 9380.2 MPa 1. Quart Kit.05 EA 9394.200 psi / -55°C (Mpa)‘ 32.6 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 355 ksi / 2.2 EA 9394S EA 9390 AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 9380™NEW! EA 9380.000 psi / 82°C (Mpa) 29.700 psi / 3.6 MPa 22.3 MPa 600 psi / 4.7 MPa 20.1 MPa 27. .50 % @ 77°F / 25°C (% at break) Compressive Strength 11. strength also make it ideal for potting.9 Mpa 35.140 psi / 3.2 EA 9394S EA 9390 AERO AERO AERO AERO AERO • Low temp curing two-part adhesive • Low temp curing two-part adhesive is a fast curing two-part structural is a two-part structural paste adhesive.9 MPa 5. Clip Pack. Gallon Kit.1 MPa 1.9 MPa 17.750 psi / 12 MPa 1.0 MPa 33.000 psi / 68.237 MPa 418 ksi / 2. Liquid Shim Liquid Shim | 49 Structural Adhesives Paste Adhesives Liquid Shim Notes Characteristics 180°F / 82°C Service • • 300°F / 149°C Service • • 350°F / 177°C Service • Improved Hot / Wet Pro- • • • perties Toughened • • • Consistency Thixotropic Thixotropic Thixotropic Thixotropic Low Viscosity Form 2 Part 2 Part 2 Part 2 Part 2 Part Peel Strength High High Nil Low Nil Mechanical Bell Peel 77°F (lb / in) 50 lbs / in 40 lbs / in 20 lbs / in 20 lbs / in – Properties 25°C (N / 25 mm) 178 N / 25 mm 220 N / 25 mm 90 N / 25 mm 90 N / 25 mm -67°F (psi) / 4. toughness and high temperature.7 MPa 15.2™ EA 9394S™ EA 9390™ Availability Dual Cartridge. filling and liquid shim applications.9 MPa 180°F (psi) / 4. • Good Hot/Wet Strength • Meter mixable • Meter mixable paste adhesive.000 psi / 3.880 MPa @ 77°F (ksi) / 25°C (MPa) Elongation – – – 1. Quart Kit – Injection Kit Quart Kit.300 psi / 2.2 MPa TENSILE LAP SHEAR 77°F (psi) / 5.70 % 2.000 psi / 2.1 MPa 10. and excellent high temperature compressive • Prebond humidity resistant • Prebond humidity resistant liquid shim applications.600 psi / 25°C (Mpa) 36.700 psi / 11.329 psi / 78. filling. Barrier Kit Clip Pack. Its thixotropic nature temperatures.05 EA 9394.05 EA 9394. Gram Kit.9 MPa 28. Its thixotropic nature and • High Shear Modulus temp resistance temp resistance makes it ideal for potting.5 MPa @ 77°F (psi) / 25°C (MPa) Tensile Modulus – – – 615 ksi / 4.500 psi / 17. toughness and high • High strength.100 psi / 4.350 psi / 5.300 psi / 78 MPa – 11.5 MPa 21.000 psi / 3.0 MPa 27. Pint Kit.200 psi / 2.200 psi / 56. Packaging Dual Cartridge.6 MPa 18.200 psi / 4. 8 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 263 ksi / 1. . adhesive.000 psi / 82.250 psi / 8.6 MPa (psi / MPa) low viscosity wet lay-up solutions. injection.500 psi / 3.000 psi / 55. Its room temperature cure • Room Temperature Storage of the mixed system allows it to be capability and low viscosity make it • High Strength at Low and High injected into pre-assembled parts. Bulk Properties Tg Dry (°F / °C) 120 °F / 49 °C 156 °F / 69 °C 208 °F / 98 °C Tg Wet (°F / °C) – – 145 °F / 63 °C Why choose LOCTITE low viscosity wet lay-up products? Tensile Strength 6.0 MPa 15. Gallon Kit. Gram Kit.750 MPa ›› Enhanced occupational safety during employee exposure times Elongation 8. The low viscosity strength. Pint Packaging Quart Kit Kit. and coating.300 psi / 45 MPa 5.5 Mpa 10. ideal for repair applications.9 MPa 1.300 psi / repairs.300 psi / 3.812 MPa 158 ksi / 1. which • Low Viscosity paste adhesive designed for bonds has excellent elevated temperature • Room Temperature Cure requiring flexibility. 5-Gallon Kit.552 MPa 400 ksi / 2. makes it useful for bonding dissimilar substrates.93 °C 77 – 150 °F / 25 – 66 °C 200 °F / 93 °C“ 8 Hours / LOCTITE low viscosity wet lay-up key features: CureTime 75 Minutes / 5 – 7 Days / 1 Hour 3 – 5 Days / 1 Hour 30 Minutes / ›› Two-component system ›› Room temperature or elevated cure 5 Minutes ›› Low viscosity ›› Ideal for OEM assembly or repair StorageTemperature (°F / °C) 77 °F / 25 °C 40 °F / 4 °C 77 °F / 25 °C Pot Life 60 Minutes / > 30 minutes / 120 Minutes / (minutes / lb) / (minutes / kg) 200 Gram Mass 450 Gram Mass 100 Gram Mass Key factors to consider when choosing the right LOCTITE low viscosity wet lay-up solution LOCTITE LOCTITE LOCTITE ›› Fiber volume ratio (55 %) ›› Fabric alignment Product New Product Name EA 9313 EA 956 EA 9396 AERO AERO AERO ›› Porosity level (<1 %) ›› Resin physical-chemical properties (viscosity) Hysol® Hysol® Hysol® Known As ›› Cure temperature ›› Pot life EA 9313™ EA 956™ EA 9396™ Availability 50-Gram Kit.040 psi / 62. Barrier Clip Pack.0 MPa 8. they provide an optimal adhering surface for subsequent painting and coating.40 % @ 77°F / 25°C (% at break) Compressive Strength 9. 77°F (psi) / 4.8 MPa 70.9 MPa 12. Henkel offers the right solution for this challenge: LOCTITE Elevated Temperature – 1.800 psi / 40.2 MPa ›› High-temperature applications @ 77°F (psi) / 25°C (MPa) Tensile Modulus ›› Long open life up to eight hours @ 77°F (ksi) / 25°C (MPa) 330 ksi / 2.8 MPa 24. Pint Kit.500 psi / 25°C (Mpa) 31.1 MPa 180°F (psi) / 500 psi / 1.150 MPa @ 77°F (ksi) / 25°C (MPa) LOCTITE laminate and wet lay up resins: Handling Mix RatioWeight (PartA / Part B) 100 : 25 100 : 58 100 : 30 Facts at a glance CureTemperature (°F / °C) 77 °F / 25 °C 100 °F / 38 °C 140 °F / 60 °C 77 – 200 °F / 25 .0 MPa With more than 50 years experience.3 MPa 12.200 psi / … and perfect surface preparation: LOCTITE low viscosity wet lay-up.780 psi / 3. Laminate and Wet Lay-up Resins Laminate and Wet Lay-up Resins | 51 Structural Adhesives Paste Adhesives Laminate and Wet Lay-up Resins 300°F/149°C Service • • Improved Hot / Wet Pro- • perties Low viscosity.000 psi / 55.500 psi / 2.00 % 2.40 % 3.000 psi / 6. It can also be used as a laminating resin and for potting small assemblies.089 MPa 8.274 MPa 370 ksi / 2. Clip Pack.000 psi / 482. including Temperatures The flexibility of the cured adhesive laminating.200 psi / 1. high quality: Toughened • • LOCTITE laminate and wet lay-up resins Consistency Form Low Viscosity 2 Part Low Viscosity 2 Part Low Viscosity 2 Part Peel Strength High Nil Moderate For high temperature applications … Mechanical Bell Peel 77°F (lb / in) 60 lbs / in 25 lbs / in – Properties 25°C (N / 25 mm) 267 N / 25 mm 111 N / 25 mm A low viscosity system is needed for high temperature wet lay-up composite construction or -67°F (psi) / 4. Quart Kit Injection Kit. 82°C (Mpa) 3.8 MPa TENSILE LAP SHEAR be employed. Curing very fast under heat. Gallon Kit.3 MPa 22. Quart Kit“ LOCTITE LOCTITE LOCTITE Description EA 9313 EA 956 EA 9396 AERO AERO AERO is a low viscosity. It should allow wet lamination processes as well as out-of-autoclave curing processes to -55°C (Mpa)‘ 28. Kit. two component is a two-component.3 MPa 22. Gram Kit. 2 MPa TENSILE LAP SHEAR 77°F (psi) / 4.600 psi / 25°C (Mpa) 31.500 psi / 17.100 psi / 82°C (Mpa) 28.7 MPa 180°F (psi) / 4.3 MPa Elevated Temperature 2. Laminate and Wet Lay-up Resins Laminate and Wet Lay-up Resins | 53 Structural Adhesives Paste Adhesives Laminate and Wet Lay-up Resins Notes Characteristics 300°F/149°C Service • Improved Hot / Wet Pro- • perties Toughened Consistency Low Viscosity Form 2 Part Peel Strength Low Mechanical Bell Peel 77°F (lb / in) 15 lbs / in Properties 25°C (N / 25 mm) 67 N / 25 mm -67°F (psi) / 2.2 MPa (psi / MPa) Bulk Properties Tg Dry (°F / °C) 226°F / 108°C Tg Wet (°F / °C) 232°F / 111°C Tensile Strength – @ 77°F (psi) / 25°C (MPa) Tensile Modulus – @ 77°F (ksi) / 25°C (MPa) Elongation – @ 77°F / 25°C (% at break) Compressive Strength 14.6 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 : 36 (PartA / Part B) CureTemperature (°F / °C) 200 °F / 93 °C CureTime 1 Hour StorageTemperature (°F / °C) 77 °F / 25 °C Pot Life 7 Hours / (minutes / lb) / (minutes / kg) 450 Gram Mass LOCTITE Product New Product Name EA 9396/C-2 AERO Hysol® Known As EA 9396™ / C-2™ Availability Packaging Quart Kit LOCTITE Description EA 9396/C-2 AERO • Low Viscosity • Long Work Life • Non-MDA Curing Agent • Ideal for use as Neat Lay-up Resin .000 psi / 96.500 psi / -55°C (Mpa)‘ 17. 000 psi / 3. It uses a non-aroma. . thermal cycling.5 MPa At the same time. although it is epoxy chemistry.0 MPa 180°F (psi) / 2. Form 2 Part 2 Part 2 Part moisture. Injection Kit. over a wide temperature range. it is a systems.3 • 0.000 psi / 5.500 psi / 17. paste adhesive. assembling and testing (PartA / Part B) CureTemperature (°F / °C) 77 – 200 °F / 25 . dust and chemicals and provide electrical Elevated Temperature ­insulation.2 MPa @ 77°F (psi) / 25°C (MPa) ›› Prevents corrosion from moisture. operating 284 ksi / 1. fill voids.000 psi / 1.900 psi / 4. dust and chemicals Compressive Modulus ›› Broad selection of product chemistries allows use with different substrates.7 MPa 24.2 ›› Reduces open time in dispensing. shock and thermal stress.960 MPa – 110 ksi / 758 MPa @ 77°F (ksi) / 25°C (MPa) ­temperatures and other environmental factors Handling Mix RatioWeight 100 :50 100 :20 100 :34. operating temperatures and other environmental factors. they protect against corrosion. Mechanical Bell Peel 77°F (lb / in) 6 lbs / in 10 lbs / in – Properties 25°C (N / 25 mm) 25 N / 25 mm“ 45 N / 25 mm“ And why LOCTITE potting and edge fill compounds do it best -67°F (psi) / 3.90 MPa – – ›› Improves mechanical strength @ 77°F (ksi) / 25°C (MPa) Elongation ›› Provide insulation @ 77°F / 25°C (% at break) 6. Bulk Properties Tg Dry (°F / °C) 230 °F / 110 °C – 248 °F / 120 °C Why choose LOCTITE potting and edge Fill compounds? Tg Wet (°F / °C) 190 °F / 88 °C – – ›› Significantly improved shelf life Tensile Strength 7.00 % – – ›› Enhances resistance to vibration and shock Compressive Strength 9.280 psi / 64. High-quality potting and edge fill products effectively Peel Strength Low Low Nil prevent corrosion and ensure the long-term integrity of your device.500 psi / LOCTITE offers a broad variety of potting and edge fill and encapsulating compounds to use with – -55°C (Mpa)‘ 20. high temperature service closed cell structure with minimum with a long pot life.48 Improved Hot / Wet Pro- perties Toughened • What potting and edge fill compounds can do for you Consistency Thixotropic Moderate Viscosity Syntactic Potting and Edge Fill and encapsulation compounds provide mechanical reinforcement to housed assemblies. Quart Kit Quart Kit.500 psi / 17.00 MPa 32.2 MPa – (psi / MPa) requirements. and smoothing. offered by aromatic amine cured insert potting.7 MPa 2. All of them improve 77°F (psi) / 4. Dual Cartridge. 25°C (Mpa) 27.0 MPa – – @ 77°F (psi) / 25°C (MPa) ›› Easy to apply Tensile Modulus 42 ksi / 2. extinguishing and its thixotropic peratures.6 MPa 34.000 psi / 220.5 MPa 9. mechanical shock and vibration. Clip Pack Gallon Kit ›› Suitable packaging configurations for application ›› Adhesive can be drilled and sanded without damage ›› No sag for vertical applications ›› Dual cure or step cure processing capability Description LOCTITE LOCTITE LOCTITE EA 9321 EA 9394/C-2 HC 3056 ›› Co-curable with sandwich assembly ›› Products available in low to medium densities AERO AERO AERO is a two-component thixotropic paste is an elevated temperature curing.000 psi / – 82°C (Mpa) 20. moisture penetration.100 psi / 49. which exhibits toughness high service temperature structural potting compound. and protect devices from the effects of exposure to chemicals.1 MPa TENSILE LAP SHEAR various substrates. soapy water rather than solvents.4 MPa 2. is a two-component low-density adhesive. clean up is with hot.93 °C > 200 °F / 93 °C 77 °F / 25 °C CureTime 5 – 7 Days / 1 Hour 1 Hour 5 – 7 Days StorageTemperature (°F / °C) 40 °F / 4 °C 77 °F / 25 °C 82 °F / 28 °C Pot Life 40 Minutes / 450 Gram Mass 7 Hours / 450 Gram Mass 60 Minutes / 70 Gram Mass LOCTITE potting and edge Fill compounds: (minutes / lb) / (minutes / kg) Facts at a glance LOCTITE LOCTITE LOCTITE Product New Product Name EA 9321 EA 9394/C-2 HC 3056 AERO AERO AERO Hysol® Hysol® SynSkin® Known As EA 9321™ EA 9394™ / C-2™ HC 3056™ LOCTITE potting and edge Fill compounds key features: Availability Packaging Clip Pack. It is self- and retains strength at elevated tem.300 psi / the mechanical strength as well as the resistance to vibration. This product cures at room tic amine curing agent that retains characteristics make it ideal for use in temperature and yields durable bonds many of the excellent properties honeycomb panels for edge close out. Because of their thermal properties they are ideally suited for aerospace t­ emperature 500 psi / 3.0 MPa 27. Potting and Edge Fill Potting and Edge Fill | 55 Structural Adhesives Paste Adhesives Potting and Edge Fill Characteristics 180°F / 82°C Service • • 300°F/149°C Service Gives you strength: 350°F / 177°C Service LOCTITE potting and edge compounds 450°F / 232°C Service Cured Density (g / cc) 1. 200 psi / 8. filling.200 psi / 8.800 psi / 40.640 psi / 11. Injection Kit. Quart Kit.329 psi / 78. Barrier Kit Cartridge Gallon Kit Dual Cartridge Kit. .6 MPa 3. which cures at room • Cures at Ambient Temperature adhesive with good compressive strength at epoxy syntactic for use on honeycomb syntactic for use on honeycomb composite temperature and possesses superior • Room Temperature Storage temperature.37 0.500 psi / 65.6 MPa 13.3 MPa 1.910 psi / 4. Pint Kit.000 psi / – – -55°C (Mpa)‘ 21.8 MPa TENSILE LAP SHEAR 77°F (psi) / 3.700 psi / 2. two-part syntactic epoxy is an intermediate density.070 psi / 55.792 MPa 615 ksi / 4.400 psi / 9. which cures at room • Potting Material paste adhesive.2 EA 9395 EA 9396.530 MPa – – 429 ksi / 2.5 MPa 10.20 % 1. It her. Gallon Kit. 5-Gallon Kit Kit.940 MPa 290 ksi / 2. • Good Compressive Strength (177 °C).5 MPa 6.7 MPa 21.3 MPa 1.6MD EA 9820 EA 9825 AERO AERO AERO AERO AERO AERO AERO is a two-component thixotropic • Good Gap Filling Capabilities is a fast curing two-part structural • Non-Metallic Filler is an easy mixing.4 MPa 22.• Outstanding Mechanical Properties makes it ideal for potting. and fairing.300 psi / 2. Gallon Kit. composite parts requiring high compressi.000 psi / 68.0 MPa – 8. Availability Barrier Kit.7 MPa – – @ 77°F (psi) / 25°C (MPa) Tensile Modulus 550 ksi / 3.6MD™ EA 9820™ EA 9825™ 55-Gallon Kit.9 MPa 29.1 MPa 10.3 MPa 20.700 psi / 4.2 EA 9395 EA 9396. Quart Kit Clip Pack.8 MPa 180°F (psi) / 2.700 psi / 2.000 psi / 3.232 psi / 84 MPa @ 77°F (psi) / 25°C (MPa) Compressive Modulus 367 psi / 2.000 psi / 94.9 MPa 11. as well reinforcing.000 psi / – 25°C (Mpa) 25.8 MPa 13. one-component epoxy paste adhesive.7 MPa 18. Gram Dual Cartridge.6MD EA 9820 EA 9825 AERO AERO AERO AERO AERO AERO AERO Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Hysol® Known As EA 934NA™ EA 9394™ EA 9394. one-component is a low-density. Pint Kit Gallon Kit.500 psi / – – 82°C (Mpa) 19. Its thixotropic nature • Thixotropic higher temperatures.0 MPa 6.300 psi / 2.5 MPa 28. Quart Kit.9 MPa 33.200 psi / 8.200 psi / 4. Its thixotropic nature and good • Long Pot Life liquid shim applications.6 MPa 15.7 MPa – – (psi / MPa) Bulk Properties Tg Dry (°F / °C) 159 °F / 71 °C 172 °F / 78 °C 158 °F / 70 °C 163 °F / 73 °C 147 °F / 64 °C – – Tg Wet (°F / °C) 235 °F / 113 °C 154 °F / 68 °C 196 °F / 91 °C 246 °F / 119 °C – – – Tensile Strength 5. Potting and Edge Fill Potting and Edge Fill | 57 Structural Adhesives Paste Adhesives Potting and Edge Fill Characteristics 180°F / 82°C Service • 300°F / 149°C Service • • • • • 350°F / 177°C Service • • 450°F / 232°C Service Cured Density (g / cc) 1. for potting. Clip Pack.3 MPa 1.800 psi / 157 MPa 12. Clip Pack.38 1. filling.300 psi / 2. Clip Pack.72 Improved Hot / Wet Pro- • • perties Toughened • • • Consistency Thixotropic Thixotropic Thixotropic Thixotropic Syntactic Thixotropic Thixotropic Form 2 Part 2 Part 2 Part 2 Part 2 Part 1 Part 1 Part Peel Strength Nil Low Nil Low Nil Nil Nil Mechanical Bell Peel 77°F (lb / in) 20 lbs / in 20 lbs / in 15 lbs / in – – – – Properties 25°C (N / 25 mm) 89 N / 25 mm“ 90 N / 25 mm“ 67 N / 25 mm“ -67°F (psi) / 3. It may also be used for fastener may also be used for fastener or attach- compressive strength make it ideal • Low Toxicity or attachment potting and panel edge ment potting and panel edge reinforcing. as for shim applications.140 psi / 3.7 MPa 24. Gallon Kit“ Quart Kit LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description EA 934NA EA 9394 EA 9394.87 0. and • Excellent Mechanical Properties ve strength at temperatures up to 350 °F at temperatures up to 350 °F (177 °C).237 MPa – 717 ksi / 4.100 psi / 3.000 MPa – – @ 77°F (ksi) / 25°C (MPa) Elongation 1.956 MPa – – – @ 77°F (ksi) / 25°C (MPa) Handling Mix RatioWeight 100 :33 100 :17 100 :27 100 :17 100 :31 – – (PartA / Part B) 250 °F / 121 °C 250 °F / 121 °C CureTemperature (°F / °C) 77 – 200 °F / 25 – 93 °C 77 – 200 °F / 25 – 93 °C 77 °F / 25 °C 77 – 150 °F / 25 – 66 °C 77 – 200 °F / 25 – 93 °C 350 °F / 177 °C“ 350 °F / 177 °C“ CureTime 5 – 7 Days / 1 Hour 3 – 5 Days / 1 Hour 24 Hours 5 Days / 1 Hour 5 – 7 Days / 1 Hour 90 – 100 Minutes / 60 – 70 Minutes 90 – 100 Minutes / 60 – 70 Minutes StorageTemperature (°F / °C) 40 °F / 4 °C 77 °F / 25 °C 77 °F / 25 °C 77 °F / 25 °C 40 °F / 4 °C 0 °F / -18 °C 0 °F / -18 °C Pot Life 40 – 50 minutes / 450 Gram Mass 90 Minutes / 450 Gram Mass 20 – 30 Minutes / 100 Gram Mass 95 – 100 Minutes / 450 Gram Mass 120 Minutes / 100 Gram Mass > 8 Hours > 8 Hours (minutes / lb) / (minutes / kg) LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name EA 934NA EA 9394 EA 9394.60 0.77 % – 2.500 psi / 44.000 psi / 20.2™ EA 9395™ EA 9396.500 psi / 1.675 psi / 46.3 MPa Elevated Temperature 1. 5-Gallon Kit. Gram Kit. parts requiring high compressive strength strength to 300 °F / 149 °C and hig. Pint Kit.7 MPa 18.1 MPa 14. 5-Gallon Packaging Dual Cartridge.60 % 2–3% – – @ 77°F / 25°C (% at break) Compressive Strength 9.8 MPa 22.800 psi / 3.3 MPa 1. Aircraft manufacturers’ demands on professional release materials are high: They LOCTITE FREKOTE mold releases can be used with following materials: require a wide range of mold releases with different characteristics to meet all needs. ceramic and composite tooling ›› Low reject rates ›› Resin film infusion ›› Automated spray application ›› Available with no volatile organic compounds (VOCs) and CFCs for improved ­sustainability With support from its authorized aerospace distribution network. Paste Adhesives | 59 Structural Adhesives Mold Release Aerospace industry has many standards: LOCTITE FREKOTE mold release materials: LOCTITE FREKOTE is the one for All facts at a glance release materials Key factors to consider when choosing the right LOCTITE mold release ›› Water-based vs. easy a­ pplication and the highest number of releases possible per application are guaranteed. they only ›› Natural & synthetic rubbers ›› Thermoplastic prepregs accept materials that comply with the most rigorous requirements – their own ones. solvent-based ›› Service temperature Choosing the right release material is not as easy as ›› Slip / release characteristics ›› Transfer characteristics you might think . phenolics and BMIs ›› Thermoset prepregs They want to be sure to apply a sustainable solution. . sealers and cleaners are based on over ›› Thermoplastic polymers ›› MRO & repair 50 years of technical experience and are the most trusted for consistent release of composite parts from tools. And last but not least.and silicone-free release agents polymerize to LOCTITE FREKOTE mold releases can be used in all composite manufacturing processes: create a low surface energy film which is durable. minimized fouling. ›› Silicones ›› Polyester resins … unless you discover LOCTITE FREKOTE. A minimal transfer to molded components. ›› Urethanes ›› Vinyl ester resins Henkel’s LOCTITE FREKOTE release agents. These wax. ›› Thermoset epoxies. chemically resistant and thermally ›› Hand lay-up ›› Filament winding stable... Henkel delivers LOCTITE FREKOTE mold release ›› Dispensing equipment available agents for aerospace customers throughout the globe. ›› Automated fiber placement & tape laying ›› Injection molding ›› Autoclave molding ›› Compression molding Why choose LOCTITE FREKOTE mold release materials? ›› Vacuum bag only molding ›› Pultrusion ›› Semi-permanent mold release bonds to mold surface for consistent release ›› Resin transfer molding ›› Rotational molding ›› Higher productivity and profitability through reduced downtime ›› Vacuum infusion processes ›› Metallic. 97 to 0. Drum. • Non-CFC • No contaminating transfer • No mold build-up • Low transfer nance costs • No mold build-up • No mold build-up • Low odor • No corrosion / oxidation of the mold surface • Minimal mold build-up . or • Better mold utilisation • Fast drying • No chlorinated solvents • No contaminating transfer • High slip • Eliminates contaminants • Polishing liquid imperfections • Non contaminating transfer • Non contaminating transfer • High gloss finish • High gloss finish • Easy application • Enhances release effectiveness • Removes cured films • No contaminating transfer • No mold build up • High thermal stability • High slip • High slip • Multiple releases • High thermal stability • Significantly lower mold mainte.775 LMS 0. Pail. Aerosol Can. Pail. Pail Can. Pail.821 to 0.755 to 0.764 LMS 0. Pail. Drum. Drum.98 to 1.715 to 0.782 LMS 0.854 LMS 0. scratches. Pail Can Can.725 LMS 0.02 LMS 25°C (g / ml) Handling 210 – 300 °F 210 – 300 °F 210 – 300 °F 210 – 300 °F 210 – 300 °F CureTemperature (°F / °C) Ambient Ambient Ambient Ambient Ambient Ambient Ambient Ambient 100 – 150 °C 100 – 150 °C 100 – 150 °C 100 – 150 °C 100 – 150 °C CureTime – – 24 Hours 60 Minutes 3 Hours 15 Minutes 30 Minutes 5 Minutes 10 minutes 5 Minutes 5 – 10 Minutes 3 Hours 12 Minutes 46 – 70 °F 46 – 70 °F 46 – 70 °F 46 – 70 °F 46 – 70 °F 46 – 70 °F 46 – 70 °F 37 – 68 °F StorageTemperature (°F / °C) 8 – 21 °C 8 – 21 °C 8 – 21 °C 8 – 21 °C 8 – 21 °C 8 – 21 °C 8 – 21 °C 3 – 20 °C Storage Time 24 Months 24 Months 12 Months 12 Months 12 Months 12 Months 12 Months 9 Months LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Product New Product Name FREKOTE PMC FREKOTE PMC 915WB FREKOTE B-15 FREKOTE 44-NC FREKOTE 55-NC FREKOTE 700-NC FREKOTE 770-NC FREKOTE C-800 AERO AERO AERO AERO AERO AERO AERO AERO Frekote® Frekote® Frekote® Frekote® Frekote® Frekote® Frekote® Frekote® Known As Aqualine® PMC™ 915WB™ B-15™ 44-NC™ 55-NC™ 700-NC™ 770-NC™ C-800™ Availability Packaging Can.745 to 0. Aerosol Can. Paste Adhesives | 61 Structural AdhesivesMold Release Mold Release Applications Mold Cleaning • • Mold Sealing • Composites Molding • • • • • Compression Molding • • • • • Casting • • • • • Vacuum Bagging • • • • • High Release • • • Filament Winding • Mechanical Appearance Clear liquid Beige-Pasty liquid Clear liquid Clear Liquid Clear Liquid Clear Liquid Clear Liquid Milky White Emulsion Properties Finish – – Gloss Matte Satin Gloss Gloss Matte Density at 77 °F / 0.76 to 0. Drum.725 LMS 0. Pail LOCTITE LOCTITE LLOCTITE LOCTITE LOCTITE LOCTITE LOCTITE LOCTITE Description FREKOTE PMC FREKOTE PMC 915WB FREKOTE B-15 FREKOTE 44-NC FREKOTE 55-NC FREKOTE 700-NC FREKOTE 770-NC FREKOTE C-800 AERO AERO AERO AERO AERO AERO AERO AERO • Easy to use • Water based polisher • Seals mold porosity. Aerosol Can.715 to 0. Aerosol Can.99 LMS 0. 1 AERO 20 LOCTITE EA 956 AERO 32. 39.2 AERO 35. 40 LOCTITE EF 562 AERO 23 LOCTITE EA 934NA AERO 32.1 LS AERO 17 LOCTITE EA 9330 AERO 30. 56 LOCTITE FREKOTE B-15 AERO 60 LOCTITE EA 9394/C-2 AERO 33. 12 LOCTITE EA 9690 AERO 8. 11. 11 LOCTITE HC 9875 Aero 20 LOCTITE EA 9673 AERO 8.3 AERO 30.05 AERO 31. 38.1 BLK AERO 17 LOCTITE EA 9323 AERO 29 LOCTITE EA 9837.1 AERO 17 . 39. 42 LOCTITE FREKOTE 700-NC AERO 61 LOCTITE EA 9394 AERO 33.1 AERO 20 LOCTITE EA 960F AERO 43 LOCTITE HC 9872.1 Aero 20 LOCTITE EA 9628 AERO 7. 56 LOCTITE EF 562SFR AERO 22 LOCTITE EA 9359.1 Aero 20 LOCTITE EA 9628H AERO 7. 51 LOCTITE EA 9396.1 BLK AERO 17 LOCTITE EA 460 AERO 22 LOCTITE EA 9837. 42. 43 LOCTITE EA 9837. 13 LOCTITE EA 9845 AERO 17 LOCTITE EA 9203 AERO 25 LOCTITE EA 9845 LA AERO 17 LOCTITE EA 9258. 47. 48.1 LS AERO 17 LOCTITE EA 7000 AERO 9. 35 LOCTITE EA 9377 AERO 47 LOCTITE EF 9899 AERO 21 LOCTITE EA 9380 AERO 31. 40. 12 LOCTITE Nomeclature LOCTITE EA 9696 AERO 9. 37 LOCTITE EF 557 AERO 21 LOCTITE EA 9330.43 LOCTITE EA 9891RP AERO 35 LOCTITE EA 9309. 48 LOCTITE FREKOTE 44-NC AERO 61 LOCTITE EA 9390 AERO 32. 47 LOCTITE EF 9835 AERO 22 LOCTITE EA 9363 AERO 40 LOCTITE EF 9840 AERO 22 LOCTITE EA 9364FR AERO 39. 37 LOCTITE EF 560 AERO 23 LOCTITE EA 9345 AERO 31. 48 LOCTITE EF 9899CF AERO 21 LOCTITE EA 9380. 49 LOCTITE FREKOTE 55-NC AERO 61 LOCTITE EA 9392 AERO 35. 49 LOCTITE FREKOTE PMC AERO 60 LOCTITE EA 9395 AERO 33. 42 LOCTITE EA 9896 WPP AERO 15 LOCTITE EA 9313 AERO 51 LOCTITE EA 9658 AREO 7. 56 LOCTITE FREKOTE PMC 915WB AERO 60 LOCTITE EA 9394. 25 LOCTITE EA 9320NA AERO 29.1 AERO 23 LOCTITE EA 9360 AERO 31. 45 LOCTITE EF 9890 AERO 21. 41. 41.6MD AERO 57 LOCTITE HC 3056 AERO 55 LOCTITE EA 9396/C-2 AERO 34. 51 LOCTITE HC 9823. 12 LOCTITE EA 9695 AERO 8. 13 LOCTITE EA Epoxy Adhesives LOCTITE EA 9820 AERO 57 LOCTITE EF Expanding Materials LOCTITE EA 9825 AERO 57 LOCTITE HC Syntactic Core LOCTITE EA 9837. 57 LOCTITE FREKOTE 770-NC AERO 61 LOCTITE EA 9396 AERO 34. 41. 11 LOCTITE HC 9872. 55 LOCTITE FREKOTE C-800 AERO 61 LOCTITE EA 9394S AERO 35. 52 LOCTITE HC 9823.1 AERO 7. 11 LOCTITE EA 9845 LC AERO 17 LOCTITE EA 9309. 38 LOCTITE EF 9833. 39.2 AERO 33. 25.1 AERO 17 LOCTITE EA 9321 AERO 29.3 AERO 30. Index | 63 Structural Adhesives Index Notes Index Products Page Products Page LOCTITE EA 2000 AERO 25 LOCTITE EA 9837.3NA AERO 37 LOCTITE EA 9895 WPP AERO 15 LOCTITE EA 9309NA AERO 34. 55 LOCTITE EA 9837. 41. 38. 8882 Tel.458.211.com/aerospace-distributor Henkel Solutions for the Aerospace Industry: www. 201203 Shanghai 52760 Huixquilucan China Edo. 928 Zhang Heng Road Centro Urbano Interlomas Pu Dong. VIC Diadema – SP Germany Australia Brazil Tel.55. Ltd. Ltd Boulevard Magnocentro No.30. 136 40589 Düsseldorf 3137 Kilsyth.30. 2016 .911 Japan Tel.457 Tel.1800 Fax: +1.458.3.: +81.3.9728. Please contact Henkel Technical Support Group for assistance and r­ ecommendation on ­specifications these products.797. Germany.: +86.6073.1851 Henkel AG & Co.21.com/aerospace The data contained herein are intended as reference only.: +49.00.8030 Fax: +81.3205.5877 Tel.211.8000 Fax: +31.12998 Fax: +61. Except as otherwise noted. Henkel Corporation Aerospace Henkel Nederland B. Kilsyth Henkel Brazil Ltda Henkelstraße 67 135-141 Canterbury Road Rua Karl Huller.45.: +1.45. Isogo-kut 2850 Willow Pass Road 3432 NZ Nieuwegein Yokohama-shi Bay Point.henkel-adhesives.21. all marks used above in this printed material are trademarks and/or registered trademarks of Henkel and/or its affiliates in the US.33.798.6054.758.925. and elsewhere.: +61.8955 ASIA-PACIFIC Henkel Mexicana Henkel (China) Co.henkel-adhesives.9724. © Henkel AG & Co. Henkel Technology Center P.30.758. De México Tel..2891.5192 Tel.11.00 Fax: +86. Box 312 ­ Brugwal 11 27-7 Shin Isogo-cho.925. O.V.6070 List of authorized distributors: www.6360.: +52..8 Piso 2 No. KGaA. AT5003015 V3 NORTH AMERICA EUROPE Henkel Japan Ltd.6444 09941-410 Fax: +49. CA 94565 Netherlands Kanagawa 235-0017 United States Tel. KGaA LATIN AMERICA Aerospace Henkel Australia Pty.: +31.: +55.